A Mg-Y-Ca-Ce magnesium alloy was optimized for high ignition-proof property,which did not burn in air at 1233 K up to30 min.Oxidation behavior of the alloy was investigated by X-ray diffraction(XRD),scanning electron microscopy(SEM),and thermodynamics calculation at 673,773 and 873 K.XRD and SEM analysis indicated that dense and compact oxide films composed of MgO,Y2O3and CaO formed.The oxidation behavior was characterized by the selective oxidation.Based on Pilling-Bedworth ratio(PBR)and energy dispersive spectrometer(EDS)analysis,Y2O3contributed more to form the compact surface oxide film,which led to the excellent ignition-proof performance.The thermodynamics analysis and EDS results implied that the Y-rich areas were preferred paths for the selective oxidation.
A Mg-Y-Ca-Ce magnesium alloy was optimized for high ignition-proof property, which did not burn in air at 1233 K up to 30 min. Oxidation behavior of the alloy was investigated by X-ray diffraction (XRD) Microscopy (SEM), and thermodynamics calculation at 673, 773 and 873 K. XRD and SEM analysis showed that dense and compact oxide films composed of MgO, Y2O3 and CaO formed. The oxidation behavior was characterized by the selective oxidation. Based on Pilling-Bedworth ratio PBR) and energy dispersive spectrometer (EDS) analysis, Y2O3contributed more to form the compact surface oxide film, which led to the excellent ignition-proof performance. The thermodynamics analysis and EDS results implied that the Y-rich areas were preferred paths for the selective oxidation.