Baivumebo iron ore is special magnetite containing fluorine,kalium and sodium elements,and the main raw material for ironmaking of Baotou Iron and Steel(Group) Co.The effects of basicity and ratio of Al2O3 to SiO2(A/S) on the formation of silico-ferrite of calcium and aluminium(SFCA) in Baivumebo low silica sinters were studied by means of mini-sintering,XPF-500 optical mineralogical microscope and CSS-88000 electronic universal testing machine.The results show that it is beneficial to the formation of complex calcium ferrite to enhance the basicity of Baivumebo low silica sinters.The acicular SFCA-I was increased with the enhancing basicity and reached the peak at basicity 2.8,then the columnar or platy SFCA formed and the bonding strength decreased.Alumina is beneficial to the formation of acicular complex calcium ferrite in Baivumebo low silica sinters.But the residual unfused Al2O3 reagent came into being when A/S was 0.35,while complex calcium ferrite still remained to be acicular.There is a common rule about mineralogy components affected by basicity and ratio of A/S,that is,SFCA is increasing accompanied with hematite and porosity reduced,but the content of glass phase is stable.
Baivumebo iron ore is special magnetite containing fluorine, kalium and sodium elements, and the main raw material for ironmaking of Baotou Iron and Steel (Group) Co. The effects of basicity and ratio of Al2O3 to SiO2 (A / S) on the formation of silico-ferrite of calcium and aluminum (SFCA) in Baivumebo low silica sinters were studied by means of mini-sintering, XPF-500 optical mineralogical microscope and CSS-88000 electronic universal testing machine. The results show that it is beneficial to the formation of complex calcium ferrite to enhance the basicity of Baivumebo low silica sinters. acicular SFCA-I was increased with the enhancing basicity and reached the peak at basicity 2.8, then the columnar or platy SFCA formed and the bonding strength decreased. Aluminum was beneficial to the formation of acicular complex calcium ferrite in Baivumebo low silica sinters.But the residual unfused Al2O3 reagent came into being when A / S was 0.35, while complex calcium ferrite still remained to be acicular .here is a common rule about mineralogy components affected by basicity and ratio of A / S, that is, SFCA is increasing accompanied with hematite and porosity reduced, but the content of glass phase is stable.