The final microstructure of DP and TRIP assisted steels can evolve after hot working (hot rolling) or during post heat treatment process. In the formation of the final structure a number of different technological parameters have important roles, e.g. end temperature of rolling, cooling rates, temperature of intercritical annealing, etc. As a result of the individual factors and their combinations a lot of product technology routes are feasible. The effect of the different combinations of these technological parameters on the microstructure can be mapped by the special Jominy end-quench test (so called intercritical Jominy end-quench test) described in this paper. Unlike the traditional Jominy test, in this case there is a partial austenizing between A! and A3 temperatures which results in a given amount of ferrite in the microstructure before quenching. The method developed can be applied for mapping DP and TRIP assisted steels’ microstructure in a wide range of technological parameters. The analysis of measured and calculated data can help us find the technological parameters optimal from the microstructural point of view.
The final microstructure of DP and TRIP assisted steels can evolve after hot working (hot rolling) or during post heat treatment process. In the formation of the final structure a number of different technological parameters have important roles, eg end temperature of rolling, cooling rates , temperature of intercritical annealing, etc. As a result of the individual factors and their combinations a lot of product technology routes are feasible. The effect of the different combinations of these technological parameters on the microstructure can be mapped by the special Jominy end-quench Unlike the traditional Jominy test, in this case there is a partial austenizing between A! and A3 temperatures which results in a given amount of ferrite in the microstructure before quenching. The method developed can be applied for mapping DP and TRIP assisted steels’ microstructure in a wide range of technological paramete rs. The analysis of measured and calculated data can help us find the technological parameters optimal from the microstructural point of view.