Through improving the aging process during synthesis of the support, γ-Al2O3 with large pore volume and high surface area was synthesized by a facile secondary reforming method. The synthesis parameters, such as the reaction temperature, the first aging temperature and the second aging temperature, were investigated. The textural properties of γ-Al2O3 were characterized by means of N2 adsorption-desorption isotherms, X-ray powder diffractometry(XRD), scanning electron microscopy(SEM), Fourier transform infrared(FTIR) spectroscopy and thermogravimetry(TG). The experimental results indicated that AACH and amorphous AlOOH were the precursors of alumina, which were formed via precipitation from solutions after reaction of aluminum sulphate with ammonium hydrogen carbonate. The precursor nanocrystallites grew and re-assembled during the secondary reforming process, which resulted in an increased pore size and pore volume and a decreased bulk density. The as-synthesized γ-Al2O3 materials featured meso/macroporosity, large pore volume(2.175 cm3/g), high surface area(237.8 m2/g), and low bulk density(0.284 g/mL). Through improving the aging process during synthesis of the support, γ-Al2O3 with large pore volume and high surface area was synthesized by a facile secondary reforming method. The synthesis parameters, such as the reaction temperature, the first aging temperature and the second aging temperature , were investigated. The textural properties of γ-Al2O3 were characterized by means of N2 adsorption-desorption isotherms, X-ray powder diffractometry (XRD), scanning electron microscopy (SEM), Fourier transform infrared (FTIR) spectroscopy and thermogravimetry . The experimental results indicated that AACH and amorphous AlOOH were the precursors of alumina, which were formed via precipitation from solutions after reaction of aluminum sulphate with ammonium hydrogen carbonate. The precursor nanocrystallites grew and re-assembled during the secondary reforming process, which resulted in the increased pore size and pore volume and a decreased bulk density. The as-synthesized γ-Al2O3 materials The characteristic pore volume (2.175 cm3 / g), high surface area (237.8 m2 / g), and low bulk density (0.284 g / mL) are the characteristics meso / macroporosity.