Silver nano-particles with average diameter of about 60 nm were compacted in a high-strength mold under different pressures at 523 K to produce nano-structured Ag solid materials. The structure and characteristic of the nano-structured Ag solid materials (NSS-Ag) were studied using X-ray diffraction (XRD), scanning electron microscope (SEM) and Raman spectrometer. The NSS-Ag could be used as highly efficient surface-enhanced Raman scattering (SERS) active substrates. The common probe molecules Rhodamine 6G (R6G, 1×10-10 mol/L) were used to test the SERS activity on these substrates at very low concentrations. It is found that the SERS enhancement ability is dependent on the density of NSS-Ag. When the relative density of NSS-Ag is 83.87%, the materials reveal great SERS signal.
Silver nano-particles with an average diameter of about 60 nm were compacted in a high-strength mold under different pressures at 523 K to produce nano-structured Ag solid materials. The structure and characteristic of the nano-structured Ag solid materials ) were studied using X-ray diffraction (XRD), scanning electron microscope (SEM) and Raman spectrometer. The NSS-Ag was used as highly efficient surface-enhanced Raman scattering R6G, 1 × 10-10 mol / L) were used to test the SERS activity on these substrates at very low concentrations. It is found that the SERS enhancement ability is dependent on the density of NSS-Ag. When the relative density of NSS -Ag is 83.87%, the materials reveal great SERS signal.