The experimental data in the MgH2-5at%V composite was summarized and used to investigate the kinetic mechanism of hydrogen absorption and desorption using a new model. The research results indicate that a coincidence of the theoretical calculation values with the experimental data has been reached and the rate-limiting step is hydrogen diffusion through the hydride phase (β phase) with the activation energy of 47.2 kJ per mole H2 for absorption and the diffusion of hydrogen in the α solid solution (α phase) with that of 59.1 kJ per mole H2 for desorption. In addition, the hydriding rate of the MgH2-V composite is 2.9 times faster than that of MgH2 powders when compared with their characteristic absorption time directly. The experimental data in the MgH2-5at% V composite was summarized and used to investigate the kinetic mechanism of hydrogen absorption and desorption using a new model. The research results indicate that a coincidence of the theoretical calculation values ​​with the experimental data has been reached and the rate-limiting step is hydrogen diffusion through the hydride phase (β phase) with the activation energy of 47.2 kJ per mole H2 for absorption and the diffusion of hydrogen in the α solid solution (α phase) with that of 59.1 kJ per mole H2 For desorption. In addition, the hydriding rate of the MgH2-V composite is 2.9 times faster than that of MgH2 powders when compared with their characteristic absorption time directly.