A full solution method has been developed as a low cost process of YBa2Cu3O7-x (YBCO) coated conductor fabrication.In this study,highly biaxially textured SrTiO3 (STO) buffer layers were fabricated on LaAlO3 (LAO) single crystal substrates by sol-gel method using metal alkoxides as the staring precursor materials.High quality YBCO superconducting film was then fabricated on STO-buffered LAO substrate by triflvoroacetic metalorganic deposition (TFA-MOD) method.For the YBCO superconducting film,only (001) diffraction peaks can be detected by XRD (X-ray diffraction) analysis with no other phases detectable.Especially,In-plane texture of YBCO film is improved compared to that of STO buffer layer from phi scans analysis,which indicates the self-epitaxy phenomenon explained by considering interfacial energy.STO and YBCO films both show c-axis oriented grains growt.h and have uniform surface microstructure.A critical transition temperature,Tc (R=0) of 89.5 K and a critical current density of 2 mA/cm2 (17 K,self-field) were obtained for a 0.2 μm thick YBCO film on STO-buffered LAO substrate.No reaction between YBCO and STO was detected by XRD analysis.This full solution process may provide a promising low cost fabrication route for YBCO coated conductors on metal tape.