【摘 要】
：
The coating of ZnS∶Mn by Sb-doped SnO2 using an co-precipitation process was reported. ZnS∶Mn phosphor particles were prepared by solid reaction with ZnS and
【机 构】
：
Chemistry and Materials Science Department
论文部分内容阅读
The coating of ZnS∶Mn by Sb-doped SnO2 using an co-precipitation process was reported. ZnS∶Mn phosphor particles were prepared by solid reaction with ZnS and MnCl2·4H2O. Surface modification of the ZnS∶Mn powders was carried out by coating transparent conductive films of Sb-doped tin oxides which were formed by co-precipitation and heat treatment process. Tin tetrachloride and antimony trichloride were used as the precursor materials for the co-precipitation. The influences of coating molar ratio, Sb concentration in the coatings, annealing temperature and time on the resistivity of coated ZnS∶Mn phosphors were investigated. The optimum co-precipitation processing parameters and annealing conditions were determined. The phosphors were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), photoluminescence(PL) observation and conductance measurements. An improvement in phosphors conductivity was observed while the respective photoluminescence intensity is analogous to the as-prepared ZnS∶Mn phosphors.
其他文献
La doped nanocrystalline TiO2 photocatalyst was developed by sol-gel method. The prepared La-TiO2 photocatalysts with anatase phases were characterized by X-ray
Computational studies of a class of potentially stable high-spin biradicals that two-atom-three-electron spin centers SC units connected by heterocycles FC and
The compressive experiments of two kinds of ceramic foams were completed. The results show that the behavior of ceramic foams made by organic filling method is
In order to improve the prediction capability of spring-back in aluminum sheet metal forming, the influence of the plastic deformation on elastic modulus is con
The ceramic coating formed on AZ91 magnesium alloy by micro-arc oxidation (MAO) was characterized. The results show that the ceramic coating(3.4-23 μm in thick
By electrical resistance tomography (ERT) the cross sectional profiles of gas hold-up in a φ56mm bubble colunmn are obtained with four designs of gas sparger.
Fouling-resistant ceramic-supported polymer composite membranes were developed for removal of oil-in-water (O/W) microemulsions. The composite membranes were fe
Free radical co-polymerization was employed to synthesize co-poly carboxylate (PC) superplasticizers with different amount of carboxyl and methyl polyethylene g
Alumina sols with a mlar ratio of 1: 50 between aluminum sec- butoxide ( ASB ) and H2 O werefabricated by adding various amounts of nitric acid.The particle sha
A laboratory study was undertaken to investigate drying shrinkage and cracking sensitivity subjected to restrained shrinkage of mortar containing fly ash (FA),