A new method for fabricating ordered porous silicon is reported.A two-dimensional silica nanosphere array is used as a template with a hydrofluoric acid-hydrogen peroxide solution for etching the nanospheres.The initial diameter and distribution of the holes in the resulting porous silicon layer are determined by the size and distribution of the silica nanospheres.The corrosion time can be used to control the depths of the holes.It is found that the presence of a SiO_2 layer,formed by the oxidation of the rough internal surface of the hole,is the primary reason allowing the corrosion to proceed.Ultraviolet reflection and thermal conductivity measurements show that the diameter and distribution of the holes have a great influence on properties of the porous silicon.
A new method for fabricating ordered porous silicon is reported. A two-dimensional silica nanosphere array is used as a template with a hydrofluoric acid-hydrogen peroxide solution for etching the nanospheres. The initial diameter and distribution of the holes in the resulting porous silicon layer are determined by the size and distribution of the silica nanospheres. The corrosion time can be used to control the depths of the holes. It is found that the presence of a SiO 2 layer, formed by the oxidation of the rough internal surface of the hole, is the primary reason allowing the corrosion to proceed. Ultraviolet reflection and thermal conductivity measurements show that the diameter and distribution of the holes have a great influence on properties of the porous silicon.