A new laser crystal Nd0.05La0.95Sc3(BO3)4 up to 50mm(38mm(7 mm was grown by top-seeded solution growth method from a Li6B4O9 flux. The grown crystal was characterized by X-ray powder diffraction. Its crystal structure is monoclinic with space group Cc and the unit cell dimensions: a=12.066(5), b=9.864(2), c=7.740(3) ?,β= 105.48(5)(, V=887.8(6)?3, Z=4, Dc=3.81g/cm3, which belongs to low-temperature phase. The optical absorption of the crystal shows that NLSB has a strong absorption band at 807.7 nm, which is suitable for laser-diode pumping.
A new laser crystal Nd0.05La0.95Sc3 (BO3) 4 up to 50 mm (38 mm (7 mm was grown by top-seeded solution growth method from a Li6B4O9 flux. The grown crystal was characterized by X-ray powder diffraction. Its crystal structure is monoclinic with space group Cc and unit cell dimensions: a = 12.066 (5), b = 9.864 (2), c = 7.740 , Z = 4, Dc = 3.81 g / cm3, which belongs to low-temperature phase. The optical absorption of the crystal shows that NLSB has a strong absorption band at 807.7 nm, which is suitable for laser-diode pumping.