论文部分内容阅读
使用选区激光熔化(SLM)技术制备了Ti6Al4V钛合金体心立方多孔结构,分别研究了线能量密度和微杆直径对体心立方多孔结构成形方向(Z向)和非成形方向(X/Y向)压缩性能的影响。结果表明,采用SLM技术成形的体心立方多孔结构存在明显的各向异性。随着线能量密度的下降,体心立方多孔结构的抗压强度先增大后减小,其各向异性程度在最优参数下达到最低。随着微杆直径的减小,体心立方多孔结构的各向异性程度逐步降低;当微杆直径降至0.4mm时,各向异性程度仅为3%左右。研究表明,即使是各向同性的多孔结构,采用SLM技术成形后,也会表现出明显的各向异性;这种各向异性与成形质量和层间界面有关,通过调整工艺参数及修改模型特征尺寸可以在一定程度上减弱这种各向异性。
The body-centered cubic porous structure of Ti6Al4V titanium alloy was prepared by selective laser melting (SLM) technique. The effects of linear energy density and micro-rod diameter on the forming direction (Z direction) and non-forming direction ) Compression performance impact. The results show that there is obvious anisotropy of the BCC structure formed by SLM technique. With the decrease of the linear energy density, the compressive strength of the cubic porous structure increases first and then decreases, and the anisotropy reaches the lowest under the optimal parameters. With the decrease of the diameter of the micro-rods, the degree of anisotropy of the body-centered cubic porous structure gradually decreases; when the diameter of the micro-rods is reduced to 0.4 mm, the degree of anisotropy is only about 3%. The results show that even the isotropic porous structure exhibits obvious anisotropy after forming by SLM technique. The anisotropy is related to the forming quality and interlayer interface. By adjusting the process parameters and modifying the model features The size can weaken this anisotropy to some extent.