The microstructure evolution during strain induced ferrite transformation was followed in thermal-simulation tests of clean 08 and 20Mn steels. The influences of carbon equivalence and initial austenite grain size on ferrite grain refinement and the volume frac- tion of ferrite during straining were inspected. The results revealed that the accelerating effect of ferrite transformation by strain was increased as the carbon equivalence decreased. However, finer ferrite grains were obtained at higher carbon content. At strain of -1 .5 ferrite grains less than 3 μm and 2 μm can be obtained in 08 and 20Mn steels respectively. Whereas the ferrite grain refinement in 08 steel was due to both effects of strain induced transformation and ferrite dynamic recrystallization, that in 20Mn was mainly due to st fain induced transformation. Heavy strain can produce fine ferrite grains in coarse austenite grained 08 steel, but it would lead to band microstructure in coarse austenite grained 20Mn.
The microstructure evolution during strain induced ferrite transformation was followed in thermal-simulation tests of clean 08 and 20 Mn steels. The influences of carbon equivalence and initial austenite grain size on ferrite grain refinement and the volume frac- tion of strained were inspected. The results revealed that the accelerating effect of ferrite transformation by strain was increased as the carbon equivalence decreased by strain was increased as the carbon equivalence decreased by strain of -1 .5 ferrite grains less than 3 μm and 2 μm in 08 and 20Mn steels respectively. Whereas the ferrite grain refinement in 08 steel was due to both effects of strain induced transformation and ferrite dynamic recrystallization, that in 20Mn was mainly due to st fain induced transformation. Heavy strain can produce fine ferrite grains in coarse austenite grained 08 steel, but it would lead to band microstructure in coarse austenite grained 20Mn .