【摘 要】
：
Steady-state corrosion and wear behaviors of two Al-bronzes, Cu-14Al-X and QAl9-4, in 5.0% H2SO4 solution were investigated. It is found that wear loss of bronz
【机 构】
：
State Key Laboratory of Advanced Non-Ferrous Materials
【出 处】
：
中国有色金属学会会刊（英文版）
【发表日期】
：
2004年期
其他文献
Influence of rare earth elements on corrosion resistance of BFe10-1-1 alloys in flowing marine water
The corrosion behavior of BFe10-1-1 alloy with different rare earth (RE) contents in simulated flowing marine water was investi-gated by X-ray diffractometer an
During deep drawing process, the material parameters of blank have a significant effect on the quality of the drawn part and the determination of process parame
Isometric heat capacity cv and isobaric heat capacity cp of Pt with stable and metastable phases were calculated by using pure element systematic theory. These
Effect of ion nitriding modification on surface hardness, corrosion resistance and magnetostriction of (Tb0.3Dy0.7)Fe1.95 alloy was investigated. Results demons
Unusual intense infrared-to-ultraviolet upconversion luminescence was observed in YF3:Yb3+(20%)/Tm3+(1%) nanocrystals under 980 nm excitation. The intense ultra
Preparation of Semisolid A356 Alloy Feedstock Cast via a Pipe Consisting of Partial Inclined and Par
In the present work, the microstructures of A356 feedstock cast via a pipe consisting of partial inclined and partial vertical sections were investigated. The e
Thermal conductivity of (Sm1-xLax)2Zr2O7 (x=0, 0.25, 0.5, 0.75 and 1) oxides for advanced thermal ba
Pyrochlore oxides of general compositions, A2Zr2O7, where A is a 3+ cation (La to Lu), are promising candidate materials for ap-plications as high temperature t
The effects of mineral processing wastewater on sulfide minerals were investigated by flotation, infrared spectrometry and electrochemistry test. The results sh
The flow and concentration fields in a new style tubular stirred reactor were simulated by simulating the fluids dynamics(CFD), in which FLUENT software was use
It iS known that the strength of alloys can be successfully improved by rapid solidification. The paper presents a process where Cu-Cr-Sn-Zn lead frame alloy is