The microstructure analysis and mechanical properties evaluation of laser beam welded AISI 409M ferritic stainless steel joints are investigated.Single pass autogeneous welds free of volumetric defects were produced at a welding speed of 3 000 mm/min.The joints were subjected to optical microscope,scanning electron fractographe,microhardness,transverse and longitudinal tensile,bend and charpy impact toughness testing.The coarse ferrite grains in the base metal were changed into dendritic grains as a result of rapid solidification of laser beam welds.Tensile testing indicates overmatching of the weld metal is relative to the base metal.The joints also exhibited acceptable impact toughness and bend strength properties. The microstructure analysis and mechanical properties evaluation of laser beam welded AISI 409M ferritic stainless steel joints are investigated. Single pass autogenous welds free of volumetric defects were produced at a welding speed of 3 000 mm / min. The joints were subjected to optical microscope, scanning electron fractographe, microhardness, transverse and longitudinal tensile, bend and charpy impact toughness testing. The coarse ferrite grains in the base metal were changed into dendritic grains as a result of rapid solidification of laser beam welds. Sensory testing indicates overmatching of the weld metal is relative to the base metal.The joints also allow impact toughness and bend strength properties.