The influence of CeO2 with different content on the thermal shock resistance of plasmasprayed Cr2O3 coating was investigated. The thermal shock failure mechanism of coating was also studied. It is found that the thermal shock failure mechanism of coating is thermal stress fatigue destruction, and the destruction takes place at interface of ceramic and bond coating. The experimental results show that the lifetime of coating fracture and failure increase considerably when 3% CeO2 is added into the plasma-sprayed Cr2O3 coating. The suitable content of CeO2 makes the microcracks exist in network form. The microcrack net can release internal stress in coating, delay the crack forming and expanding and decrease holes in coating. Thus the thermal shock resistance increase largely. The influence of CeO2 with different content on the thermal shock resistance of plasmasprayed Cr2O3 coating was investigated. The thermal shock failure mechanism of coating was also studied. It is found that the thermal shock failure mechanism of coating is thermal stress fatigue destruction, and the destruction The experimental results show that the lifetime of coating fracture and failure increase considerably when 3% CeO2 is added into the plasma-sprayed Cr2O3 coating. The suitable content of CeO2 makes the microcracks exist in network form . The microcrack net can release internal stress in coating, delay the crack forming and expanding and reducing holes in coating. Thus the thermal shock resistance increase largely.