本文对7050铝合金的锻造工艺塑性进行了研究。研究结果表明该合金的最佳均匀化制度是465±5℃,24～30小时;最佳锤锻温度为420～280℃。铸锭的过烧温度为490℃。
In this paper, 7050 aluminum alloy forging plasticity were studied. The results show that the best homogenization system of the alloy is 465 ± 5 ℃, 24 ~ 30 hours; the best forging temperature is 420 ~ 280 ℃. Overburn temperature of the ingot was 490 ° C.