【摘 要】
：
Sintered Sm(CobalFexCu0.1Zr0.03)7.5 (x=0.09-0.21) permanent magnets with higher Fe content were found to have higher remanence Br and maximum energy product (BH
【机 构】
：
State Key Laboratory of Electronic Thin Films and Integrated Devices,Shcool of Materials Science and
论文部分内容阅读
Sintered Sm(CobalFexCu0.1Zr0.03)7.5 (x=0.09-0.21) permanent magnets with higher Fe content were found to have higher remanence Br and maximum energy product (BH)max at room temperature. Br and (BH)max reached maximum of 0.96 T and 176.7 kJ/m3, respectively at room temperature when the Fe content x reached 0.21. However, the intrinsic coercivity Hci at room temperature increased gradually when the Fe content x increased from 0.09 to 0.15, but when x further increased to 0.21, Hci decreased. Hci attained its peak value of 2276.6 kA/m with Fe content x=0.15 at room temperature. For magnets with x=0.15, Br, (BH)max and Hci reached 0.67 T, 81.2 kJ/m3 and 509.4 kA/m at 500℃, respectively, showing good high temperature stability, which could be used in high temperature applications.
其他文献
唐山市中心区地质环境条件非常复杂.旧城改造和新区建设过程中,必须正确认识和评价该区域的环境地质问题,做好防减灾工作.本文分析该区域存在的地震、岩溶塌陷、采空塌陷、地
自2009年到2011年,入海口南北两岸各设立三个井水取样点,一年两次采集水样,记录水位情况,检测分析其氯度、矿化度和pH值。数据分析表明,越靠近大海,海水入侵的情况越为严重;
The semi-solid slurry of A356 alloy was prepared by low superheat pouring and slightly electromagnetic stirring, in which a pure copper rod was used to produce
通过岩体结构调查、渗透张量计算和压水试验研究岩体渗透性能.结果发现,基岩裂隙潜水活跃带距地表70 m,是有毒元素向河流迁移的活跃通道,须采取河流改道、防渗等应急措施.地
在研究区域构造的基础上,通过实测地质剖面、采集定向标本、室内薄片观察、显微构造观测和岩组分析,研究地质构造对滑坡的控制作用。结果表明,宽大的北西向石狮村韧性剪切带
Isothermal and cyclic oxidizing behavior of Co-40Cr alloy and its lanthanum ion-implanted samples were studied at 1000℃ in the air by thermal-gravimetric analy
在分析西南喀斯特石山地区石漠化现状的基础上,认为这些地区所要建立的人地关系地域系统是耗散结构.根据耗散结构理论,建立和谐的人地关系地域系统,不仅需要不断地进行物质、
Based on the needs of green motor oil, and in order to improve the antioxidation properties of green lubricating oil, the effect of tocopherol antioxidation pro
In the squeeze casting process, loaded high pressure (over approximately 100 MPa) and high temperature influence the thermo-mechanical behavior and performance