一、前言 随着电子工业的迅速发展,对硅钢薄带的性能提出了更高的要求,而硅钢薄带的性能与其晶体结构有着密切的关系。在生产硅钢薄带过程中影响其性能的工艺因素很多,本文仅选取含3wt%Si具有戈斯织构0.30毫米厚的带钢冷轧至0.10毫米厚。然后讨论在不同温度退火下0.10毫米厚冷轧带钢所获得的磁性能及其织构形成的过程,发现0.10毫 I. Introduction With the rapid development of electronic industry, the performance of silicon steel strip puts forward higher requirements. The performance of silicon steel strip has a close relationship with its crystal structure. In the process of producing silicon steel ribbons, the process of affecting the performance of many factors, this paper only selected 3wt% Si with Goss texture 0.30 mm thick strip cold rolled to 0.10 mm thick. Then we discuss the magnetic properties obtained during cold rolling of 0.10 mm thick annealed at different temperatures and the texturing process. It was found that 0.10 mm