利用自主研发的连铸机结晶器喂钢带装置在连续浇注的过程中进行了喂钢带试验。结果表明:钢带在恒温钢液中的熔化过程分为两个阶段,开始时钢带残余厚度随喂入时间的增加而快速增加,钢带厚度达到最大值后开始缓慢减小,直到钢带在钢液中全部熔化。结晶器连续浇注喂钢带工艺借助中间等轴晶的拓宽和中心偏析的分散,改善了铸坯的宏观结构。 Using self-developed caster mold feeding steel strip device in the process of continuous casting feed strip test. The results show that the melting process of steel strip in the molten steel at constant temperature is divided into two stages. At the beginning, the residual thickness of steel strip increases rapidly with the increase of feeding time. When the strip thickness reaches the maximum value, it slowly decreases until the strip In molten steel all melted. Continuous pouring mold steel feed process with the middle of the equiaxed crystal broadening and segregation of center segregation, to improve the macro-structure of the slab.