Ni3Al intermetallic was synthesized by hot pressing from element powders of nickel, aluminum, and boron. The influences of parameters on the properties of Ni3Al
【机 构】
：
School of Materials Science and Engineering
论文部分内容阅读
Ni3Al intermetallic was synthesized by hot pressing from element powders of nickel, aluminum, and boron. The influences of parameters on the properties of Ni3Al were investigated. The parameters include the particle size of nickel powder, adding or without boron powder, hot pressing temperature, etc. The properties include the density of hot-pressed samples, resultant ratio of Ni3Al phase, and bending strength. The microstructures of hot-pressed samples were investigated by X-ray diffraction and scan electronic microscopy, and the properties, such as density and bending strength, were also measured. The results show that a higher bending strength was obtained under the same hot pressing conditions by the fine nickel powder than the coarse one, and there is little difference about density. Boron powder added in this process accelerates the formation of Ni3Al and markedly increases the hot pressed density. In the temperature range of this study, the density increases along with the hot pressing temperature. Full dense Ni3Al samples were obtained under the condition of 860 ℃, 10 min, 45 MPa from Ni-22.89Al-0.5B powder.
其他文献
The experiment of ultrasonic treatment of roll casting aluminum strip on plane twin-roll cast-roller with double-heads ultrasonic tools was carried out, and the
With the hypothesis that all independent degrees of freedom of basic building blocks should be treated equally on the same footing and correlated by a possible
A two-stage process has been developed to generate the silica-based macromonomer through surface-modification of silica with polymerizable vinyl groups. The sil
Multi-failures are possible to appear in the process of using the structural system,such as dead load failure, fatigue failure and stiffness failure. The expres
A multi-stage influence diagram is used to model the pilots sequential decision making in one on one air combat.The model based on the multi-stage influence dia
Spherical cobalt blue particles with good reflectivity characteristics were synthesized by spray pyrolysis. Two different spray solutions were prepared to inves
A γ-Al2O3 particles reinforced Al-Si alloy matrix composite was fabricated by adding NH4Al(SO4)2 to molten aluminum alloy. TEM observation shows that in-situ
In the wireless guidance system,the signals that receiver received has obvious Doppler shift for the high dynamic characteristic of the carrier.A new solution o
Nonlinear dynamics of liquid-filled rectangular tank with elastic appendages are studied. Based on the assumption of ideal fluid, the coupling dynamic equations
Cu-Cr-O nanocomposites that can be used as additives for the catalytic combustion of AP(ammonium perchlorate)-based solid-state propellants were synthesized via