The hexagonal BaLa x Fe 12- x O 19 fine powders with M type structure were synthesized by sol gel method. The pH of the solution, the molar ratio of nitrate to citric acid and the calcination temperature were investigated to clarify the forming conditions of the ferrites. The crystal structure, grain size, form and magnetic properties were studied by means of XRD, SEM and vibrating sample magnetometer. It is concluded that at pH of 7.0 or so, molar ratio of nitrate to citric acid of 1/3 and calcination temperature of 850 ℃(1 h), 1 000 ℃, M type BaLa x Fe 12- x O 19 fine powders with a particle size of less than 300 nm was obtained. [
The hexagonal BaLa x Fe 12- x O 19 fine powders with M type structure were synthesized by sol gel method. The pH of the solution, the molar ratio of nitrate to citric acid and the calcination temperature were investigated to clarify the forming conditions of the ferrites. The crystal structure, grain size, form and magnetic properties were studied by means of XRD, SEM and vibrating sample magnetometer. It is concluded that at pH of 7.0 or so, molar ratio of nitrate to citric acid of 1/3 and calcination M type BaLa x Fe 12-x O 19 fine powders with a particle size of less than 300 nm were obtained at a temperature of 850 ° C (1 h) at 1000 ° C [