【摘 要】
：
Here we present an economical ambient pressure drying method of preparing monolithic silica aerogels from methyltrimethoxysilane precursor while using sodium bi
【机 构】
：
School of Engineering,Newcastle University,Newcastle upon Tyne NE1 7RU,UK;Department of Physics,Univ
论文部分内容阅读
Here we present an economical ambient pressure drying method of preparing monolithic silica aerogels from methyltrimethoxysilane precursor while using sodium bicarbonate solution as the exchanging solvent.We prepared silica aerogels with a density and a specific surface area of 0.053 g·cm-3 and 423 m2·g-1,respectively.The average pore diameter of silica aerogels is 23 nm as the pore specific volume is 1.11 cm3·g-1.Further,the contact angle between water droplet and the surface of silica aerogels in specific condition can be as high as 166°,which indicates a super-hydrophobic surface of aerogels.
其他文献
针对目前奈奎斯特采样方式对信号进行采集所产生的数据量较大的问题,提出一种基于压缩感知并结合神经网络的滚动轴承故障信号检测方法,通过K-奇异值分解算法构造冗余字典,利用神经网络以映射后观测矩阵的前一部分值预测全部观测值,实现信号的二次压缩,最终利用子空间追踪算法基于预测出的观测矩阵对信号进行重构,通过重构信号频谱可获得轴承故障信息.经过对测量矩阵、算法参数及神经网络等内容的分析,可在较少的数据量下以较高精度实现对滚动轴承故障信息的提取,并通过仿真对比实验证明了方法的有效性,在总压缩比为0.72~0.92时,
持续雾霾天气给北京电网在新形势下的安全可靠运行提出了污染新问题与安全新挑战.为研究雾霾天气下北京地区外绝缘积污特性及其对电网输变电设备的影响,本文通过研究北京地区
采用高温固相法一步合成掺杂钠型碳包覆Li1-xNaxMnPO4纳米材料,利用现代仪器分析手段表征了材料的物相、形貌和晶体结构,并考察了其作为锂离子电池正极材料的电化学性能. XRD分析结果表明,钠的掺杂没有改变LiMnPO4材料的橄榄石型正交结构,样品的结晶度好、纯度较高;SEM分析结果显示,随着钠含量的增加,样品粒径逐渐减小,当钠含量为20%时,颗粒直径减小到50 nm;TG分析结果说明,在样品制备过程中采用550℃的煅烧温度完全可行;B
Photocatalytic membranes have received increasing attention due to their excellent separation and photodegradation of organic contaminants in wastewater.Herein,
为了提升基本Boost变换器的电压增益,降低开关器件电压应力,提出一种基于耦合电感倍压的有源开关电感高增益变换器。变换器中两个耦合电感的原边组成有源开关电感结构,并引入二极管-电容支路作为无源钳位回路用来吸收漏感能量。利用变换器漏感等效电路模型分析了变换器工作模态,采用伏秒积平衡方法推导得到了变换器电压增益,并给出开关管和二极管电压应力。分析表明,两个耦合电感倍压单元可提升变换器的电压增益,耦合电感匝数比越大、耦合度越大,电压增益也越高,开关管的电压应力也越低。实验样机测试结果验证了理论分析的正确性,表明
Hydrogen fuel has been embraced as a potential long-term solution to the growing demand for clean energy.A membrane-assisted separation is promising in producin
We demonstrate the fabrication of a new DNA sensor that is based on the optical interactions occurring between oligonucleotide-coated NaYF4:Yb3+;Er3+upconversio
Propositional logic[1]is basic,based on which other logics are developed.The deduction system for propositional logic is monotonic.rnNonmonotonic logics are a c
采用SBR反应器经过5个阶段约90天的培养,驯化出以亚硝酸盐为电子受体的亚硝酸盐型反硝化聚糖菌(denitrifying glycogen accumulating organisms,DGAOs),其最大耐受NO2--N浓度约为25mg/L.驯化的亚硝酸盐型DGAOs是具有反硝化能力的一种聚糖菌(glycogen accumulating organisms,GAOs),但长期保持厌氧/缺氧环境会使其失去聚糖和反硝化能力.在进水C/N比为6的条件下,厌氧阶段C
为了研究大连地铁5号线后盐站深基坑止水帷幕优化方案,运用Midas GTS NX有限元分析软件建立不同止水帷幕的数值计算模型,分析了不同止水帷幕深度、厚度和渗透系数对稳态渗流场的影响,进一步分析了总水头、孔隙水压力、流速及渗流路径的变化规律.研究结果表明:止水帷幕深度与基坑深度比为1.22时,止水帷幕达到最佳的截水防渗作用;止水帷幕厚度与基坑抗突涌稳定性存在正相关关系,渗流流速随着厚度的增大而减慢,但厚度超过1.0 m后无显著现象;止水帷幕的渗透系数与基底水力梯度呈现负相关,但随着渗透系数的减小致使水力梯