Bi0.9Ba0.1FeO3(BBFO)/La2/3Sr1/3MnO3(LSMO) heterostructures are fabricated on LaAlO3(100) substrates by pulsed laser deposition. Giant remnant polarization value(～ 85 μC/cm2) and large saturated magnetization value(～ 12.4 emu/cm3) for BBFO/LSMO heterostructures are demonstrated at room temperature. Mixed ferroelectric domain structures and low leakage current are observed and in favor of enhanced ferroelectric properties in the BBFO/LSMO heterostructures. The magnetic field-dependent magnetization measurements reveal the enhancement in the magnetic moment and improved magnetic hysteresis loop originating from the BBFO/LSMO interface. The heterostructure is proved to be effective in enhancing the ferroelectric and ferromagnetic performances in multiferroic BFO films at room temperature.
The Bi0.9Ba0.1FeO3 (BBFO) / La2 / 3Sr1 / 3MnO3 (LSMO) heterostructures were fabricated on pulsed laser deposition of LaAlO3 (100) substrates by pulsed laser deposition (~ 85 μC / cm2) emu / cm3) for BBFO / LSMO heterostructures are demonstrated at room temperature. Mixed ferroelectric domain structures and low leakage currents are observed and in favor of enhanced ferroelectric properties in the BBFO / LSMO heterostructures. The magnetic field-dependent magnetization measurements reveal the enhancement in the magnetic moment and improved magnetic hysteresis loop originating from the BBFO / LSMO interface. The heterostructure is proved to be effective in enhancing the ferroelectric and ferromagnetic performances in multiferroic BFO films at room temperature.