Poly(L-lactide-co-caprolactone)(85-15)[P(LLA-CL)(85-15)] was synthesized from high purity L-lactide and ε-caprolactone using tin octoate as initiator by ring-opening polymerization, and characterized by infrared spectrum and 1H-NMR spectrum. The synthesized P(LLA-CL)(85-15) is a random copolymer. The influences of polymerization temperature, polymerization time, dosage of initiator and polymerization pressure on the weight average molecular weight and the polydispersity index of P(LLA-CL)(85-15) were investigated. The optimum preparation conditions of P(LLA-CL)(85-15) are: the polymerization pressure is less than 0.5 Pa, the polymerization temperature is 130 ℃, the n(M)/n(I) ratio is 8 000/1, and the polymerization time is 36 h. Under the condition, the weight-average molecular weight of prepared P(LLA-CL)(85-15) is 65.6×104, and molecular weight distribution coefficient is 1.15.
Poly (L-lactide-co-caprolactone) (85-15) [P (LLA-CL) (85-15)] was synthesized from high purity L-lactide and ε-caprolactone using tin octoate as initiator by ring- opening polymerization , and characterized by infrared spectrum and 1H-NMR spectrum. The synthesized P (LLA-CL) (85-15) is a random copolymer. The influences of polymerization temperature, polymerization time, dosage of initiator and polymerization pressure on the weight average molecular The optimal preparation conditions of P (LLA-CL) (85-15) are: the polymerization pressure is less than 0.5 Pa, the polymerization temperature is 130 ° C, the n (M) / n (I) ratio is 8 000/1, and the polymerization time is 36 h. Under the condition, the weight- average molecular weight of prepared P (LLA- CL) 15) is 65.6 × 104, and the molecular weight distribution coefficient is 1.15.