【摘 要】
：
The phase evolution,microstructure and magnetic properties of Nd9-xYxFe72Ti2Zr2B1s(x=0,0.5,1,2)nanocomposite ribbons were investigated.It was found that substit
【机 构】
：
Institute of Powder Metallurgy,State Key Laboratory for Advanced Metals and Materials
论文部分内容阅读
The phase evolution,microstructure and magnetic properties of Nd9-xYxFe72Ti2Zr2B1s(x=0,0.5,1,2)nanocomposite ribbons were investigated.It was found that substitution of Y enhanced glass forming ability of the over-quenched ribbons and stabilized the amorphous phase during post annealing treatment.Appropriate content of Y substitution effectively refined the microstructure and enhanced the remanence of the annealed samples.The residual amorphous intergranular phase in the annealed sample improved the squareness of loops,resulting in enhanced maximum energy product.The optimum annealing treatment significantly improved magnetic properties of the Y substituted ribbons.Best magnetic properties,Jr=0.78 T,Hci=923.4 kA/m,(BH)max=98.5 kJ/m3 were obtained from Nd8YFe72Ti2Zr2B15 ribbon spun at Vs= 4 m/s,and annealed at 700 ℃ for 10 min.
其他文献
Europium-doped barium thioaluminate sputtering target was synthesized by powder sintering method and thin film was deposited by radio frequency (RF) sputtering.
Polycrystalline Nd3+ and La3+ co-doped yttria nanopowder Nd3+:Y1.90La0.10O3 for transparent ceramics was synthesized by co- precipitation method using oxalate a
Melt-spun Nd7Fe90B3 ribbons were prepared under different melt treatment conditions,i.e.,the melt temperature was varied prior to ejection onto the quenching wh
Glasses with chemical composition of(in mol.%): 26 RF-20 PbO-10 TeO2-43 H3BO3-1 EuO3 (RLTB) were prepared by conven-tional melt quenching method. The Judd-Ofelt
For further improving the rate properties of Nd0.8Mg0.2(Ni0.8Co0.2)3.8 hydrogen storage alloy,the alloy was annealed in high magnetic fields(10 T).The results s
Different phases of Mg-Li-Sm alloys were prepared by galvanostatic electrolysis in LiCl-KCl-MgCl2-SmCl3 melts at 670 ℃.The electrolysis process and phase contr
Density functional theory (DFT) calculations were carried out on the compounds Cp2Ln-guan for Ln=Y, Lu, Yb, Dy and Gd, [guan=(iPrN)2CN(iPr)2]. The results were
土壤蓝藻结皮在干旱和半干旱地区广泛分布.沙埋是生长在流动沙丘表面的植物面临的重要的环境因子.实验研究了温室条件下干燥沙子不同掩埋时间(0,5,10,15,20,30天)和深度(0,0.2,0.5,1,2cm)对人工藻结皮生物量、叶绿素荧光活性和胞外多糖的影响.结果表明:大体上随着沙埋时间的延长和深度的增加人工藻结皮的F_v/F_m值和胞外多糖含量逐渐降低,但是在20天和30天沙埋处理之间,两者在不
As a mixed conductor,LaSr3Fe3O10-δ with triple layer perovskite intergrowth structure can be used as an oxygen separation membrane material and cathode materia