论文部分内容阅读
摘 要：随着经济的发展，为了有效保护耕地和生态环境，促进循环经济发展，要求在新建住宅工程中全面禁止使用粘土砖，一些以粉煤灰、煤矸石等为原料的新型墙体材料得到广泛应用。而混凝土多孔砖作为新型墙体材料的一种，在建筑结构工程中完全可以替代各类粘土砖。但近几年用混凝土多孔砖建成的住宅墙体多有裂缝发生，而这种裂缝的发生已经是一种普遍性的问题，它不仅影响到建筑物的正常使用，缩短了使用年限，而且对抗震极为不利。尤其是在住宅商品化的今天，这个问题已日益引起开发商和有关部门的普遍关注。
关键词：混凝土多孔砖；裂缝成因；防治措施
Abstract: With the development of economy, in order to protect the cultivated land and ecological environment, promote the development of circular economy, requires a total ban on the use of clay bricks in new residential projects, some new wall material with fly ash, coal gangue as raw materials are widely applied. But in recent years the use of residential concrete perforated brick walls built many cracks, and the cracks is a common problem, it not only affects the normal use of the building, shorten the service life, but also extremely detrimental to the earthquake. Especially in the commercialization of residential today, this problem has caused widespread concern of developers and related departments.
Key words: concrete perforated brick; cracks; prevention measures
中圖分类号：TU522.3+1文献标识码：A 文章编号：2095-2104（2013）
引言
在建筑工程中应用混凝土多孔砖这种新型墙体材料，无论是混凝土多孔砖的生产单位、还是使用混凝土多孔砖的建筑施工单位混凝土多孔砖都必须抓好混凝土多孔砖生产和施工的各个环节的质量控制。混凝土多孔砖的生产单位，必须按照规范标准的要求进行混凝土多孔砖的生产和出厂检验，使用混凝土多孔砖的建筑施工单位，应加强混凝土多孔砖的进场验收和施工时的正确砌筑，否则混凝土多孔砖砌体产生裂缝将是不可避免的。
一、混凝土多孔砖墙体裂缝形式
1.窗台处竖向裂缝。由于窗台处墙体较窗间墙薄，受环境变化影响大，墙体收缩受窗间墙约束，在墙体中产生拉应力，产生竖向裂缝。
2.圈梁与墙体相连处水平裂缝。在建筑物勒脚、封檐处，由于受冻融循环和干湿交替变化影响，墙体和圈梁之间易产生水平收缩裂缝。
3.门窗洞口过梁上部产生竖向裂缝。洞口过梁上部，由于墙体截面较小，在受荷载特别是施工荷载较大而墙体强度还没达到要求时，过早承受较大荷载又加上受干缩影响，就容易在过梁端部以上墙体出现裂缝。
二、混凝土多孔砖墙体裂缝的主要成因
1.材料方面
混凝土多孔砖本身的质量问题
（1）砌筑上墙的混凝土多孔砖强度没有达到设计要求的强度或产品标准的最低强度要求（即不足MUl0）；
（2）混凝土多孔砖上墙前的养护时间没有达到规定的要求（即正常情况下28d），混凝土多孔砖硬化过程中的收缩没有基本稳定；
（3）混凝土多孔砖曾被雨淋浸水，上墙时砖含水分过高，砌筑施工时发生游砖或砌筑上墙后干燥收缩。
2.设计方面
（1）混凝土多孔砖和小型空心砌块墙体对地基不均匀沉降反映非常敏感，设计中如果对地基不均匀沉降估计不足，易在墙体中产生阶梯形裂缝及底层窗台墙体的竖向裂缝。
（2）在檐口处没有保温措施，导致顶层横墙产生阶梯形裂缝。
（3）随意选择屋面保温材料而不考虑减少温差的作用，也会导致裂缝的产生。
（4）在混凝土柱与混凝土多孔砖和小型空心砌块的相接处，缺乏相应的控制裂缝措施，也会导致裂缝的产生。
3.施工方面
施工时砌筑操作不规范，没有按照《混凝土多孔砖建筑技术规程》进行施工，没有按照《砌体工程施工质量验收规范》（GB50203）和根据混凝土多孔砖的特性进行施工质量控制。
（1）砌筑时砖块的组砌方法不准确或铺浆不饱满。
（2）砌筑砂浆的稠度较大或混凝土多孔砖含水率较高，砌筑施工时发生了游砖。
（3）墙面粉刷时没有清除墙面浮灰，没有涂刷界面剂或涂刷纯水泥浆，造成粉刷层脱壳开裂。
（4）粉刷层过厚，造成粉刷层因自重开裂或空鼓开裂。
（5）砌筑施工时每日的砌筑高度过高，砌体在砖自重作用下砂浆灰缝压缩下沉，从而引起墙体的裂缝。
（6）砖墙没有按规定设置构造柱，墙体长度过长而产生收缩裂缝。
（7）砌体施工时，墙柱、墙粱以及门窗洞口边等关键部位的施工方法不准确，在墙柱间因墙体结构收缩时没有可靠拉接而产生裂缝、在墙粱间因墙体下沉而产生裂缝、门窗洞口因没有实砌砖块而安装不牢门窗的问题。
（8）砖墙转角处和纵横墙交接处等复杂受力处的墙体没有同时砌筑，或没有设置构造柱，造成砌体在砌筑时就产生了施工间断的间隙缝。
（9）粉刷层强度远高于砌体强度，在粉刷层和砌体间的界面应力下，引起粉刷层龟裂。
三、墙体裂缝防治措施
1.材料方面
（1）混凝土多孔砖、小型空心砌块产品质量应符合JC 943-2004《混凝土多孔砖》、GB 8239《普通混凝土小型空心砌块》及GB/T15229《轻集料混凝土小型空心砌块》标准的规定，其抗冻性指标必须符合国家标准的相关规定。施工时所用产品的龄期必须超过28d。产品应有产品出厂合格证和检验报告，进场后还应进行抽样复检。复检的项目应包括尺寸偏差、外观质量和强度等级等，必须先符合设计要求。
（2）混凝土多孔砖和小型空心砌块墙体应采用粘结性好、保水性好的专用砂浆砌筑，其技术性能指标应符合JC 860《混凝土小型空心砌块和混凝土砖砌筑砂浆》标准的规定，强度等级必须符合设计要求。
2.设计方面
（1）混凝土多孔砖、小型空心砌块墙体应设伸缩缝，间距不宜大于40m。
（2）防治顶层墙体裂缝的关键是降低屋面与墙体之间的温度差。因此必须同时设保温层，在檐口处的保温层应满铺，不得出现空档。在屋盖适当部位应设置分隔缝。
（3）混凝土多孔砖、小型空心砌块墙体内外墙交接处和纵横墙交接处，应沿高度每600mm设拉结钢筋，其中在顶层、底层、门窗洞口上下，拉结钢筋宜适当加密。
（4）混凝土多孔砖、小型空心砌块墙体与后砌填充墙，应沿高度每600mm设置拉结钢筋网片。
（5）提高顶层混凝土多孔砖和小型空心砌块及砌筑砂浆的强度等级，增强顶层墙体的抗拉、抗剪强度。
（6）在各层窗台处均设置钢筋混凝土窗台梁，以减少由于压力差引起的裂缝，同时提高底层窗台下砌筑砂浆的强度等级。
（7）有可能产生基础不均匀沉降的工程，可适当增加基础圈梁的刚度，以控制裂缝的产生。
3.施工方面
（1）砌筑工人应持证上岗，无上岗证者不得上岗。上岗前应做好技术交底，要求每一层的同部位墙体应由同一人施工。
（2）墙体所使用混凝土多孔砖、小型空心砌块的生产厂家必须具有准用证。砌筑前，应将混凝土多孔砖和小型空心砌块表面的污物清除，不得使用未到28d龄期或潮湿的混凝土多孔砖和小型空心砌块进行砌筑。断裂的混凝土多孔砖和小型空心砌块不得使用。
（3）砌筑水平灰缝时用座浆法铺浆，砌筑竖缝时先将混凝土多孔砖和小型空心砌块端面朝上铺满砂浆，然后上墙挤坚，并用瓦刀在竖缝中插捣密实，做到随砌随勾缝，以保证墙体有足够的抗拉、抗剪强度。若需要移动已砌好的砌体或被撞动的混凝土多孔砖和小型空心砌块，应重新铺浆砌筑。
（4）配制砂浆的原材料必须符合要求，设计配合比应有良好的和易性，砂浆稠度宜控制在50mm-70mm，施工配合比必须准确，保证砂浆强度达到设计要求。
（5）顶层的内粉刷应在屋面施工完毕后进行，以降低温差的影响。内、外墙的粉刷宜在砌体工程完工，并在墙体干缩基本稳定后施工，以防止粉刷开裂。
四、结束语
在建筑工程中应用混凝土多孔砖这种新型墙体材料，无论是混凝土多孔砖的生产单位、还是使用混凝土多孔砖的建筑施工单位混凝土多孔砖都必须抓好混凝土多孔砖生产和施工的各个环节的质量控制。通过对混凝土多孔砖的生产工艺过程和施工现场的严格管理，并在结构设计时采取综合性预防措施，就能够达到预防和减少混凝土多孔砖墙体产生裂缝的目的。
参考文献：
[1]刘立新,田高燕等.混凝土多孔砖干燥收缩性能研究[J].新型建筑材料.2008.
[2]王书祥,任泉昌.混凝土多孔砖砌体力学性能试验研究.[J]新型建筑材料.2006.
关键词：混凝土多孔砖；裂缝成因；防治措施
Abstract: With the development of economy, in order to protect the cultivated land and ecological environment, promote the development of circular economy, requires a total ban on the use of clay bricks in new residential projects, some new wall material with fly ash, coal gangue as raw materials are widely applied. But in recent years the use of residential concrete perforated brick walls built many cracks, and the cracks is a common problem, it not only affects the normal use of the building, shorten the service life, but also extremely detrimental to the earthquake. Especially in the commercialization of residential today, this problem has caused widespread concern of developers and related departments.
Key words: concrete perforated brick; cracks; prevention measures
中圖分类号：TU522.3+1文献标识码：A 文章编号：2095-2104（2013）
引言
在建筑工程中应用混凝土多孔砖这种新型墙体材料，无论是混凝土多孔砖的生产单位、还是使用混凝土多孔砖的建筑施工单位混凝土多孔砖都必须抓好混凝土多孔砖生产和施工的各个环节的质量控制。混凝土多孔砖的生产单位，必须按照规范标准的要求进行混凝土多孔砖的生产和出厂检验，使用混凝土多孔砖的建筑施工单位，应加强混凝土多孔砖的进场验收和施工时的正确砌筑，否则混凝土多孔砖砌体产生裂缝将是不可避免的。
一、混凝土多孔砖墙体裂缝形式
1.窗台处竖向裂缝。由于窗台处墙体较窗间墙薄，受环境变化影响大，墙体收缩受窗间墙约束，在墙体中产生拉应力，产生竖向裂缝。
2.圈梁与墙体相连处水平裂缝。在建筑物勒脚、封檐处，由于受冻融循环和干湿交替变化影响，墙体和圈梁之间易产生水平收缩裂缝。
3.门窗洞口过梁上部产生竖向裂缝。洞口过梁上部，由于墙体截面较小，在受荷载特别是施工荷载较大而墙体强度还没达到要求时，过早承受较大荷载又加上受干缩影响，就容易在过梁端部以上墙体出现裂缝。
二、混凝土多孔砖墙体裂缝的主要成因
1.材料方面
混凝土多孔砖本身的质量问题
（1）砌筑上墙的混凝土多孔砖强度没有达到设计要求的强度或产品标准的最低强度要求（即不足MUl0）；
（2）混凝土多孔砖上墙前的养护时间没有达到规定的要求（即正常情况下28d），混凝土多孔砖硬化过程中的收缩没有基本稳定；
（3）混凝土多孔砖曾被雨淋浸水，上墙时砖含水分过高，砌筑施工时发生游砖或砌筑上墙后干燥收缩。
2.设计方面
（1）混凝土多孔砖和小型空心砌块墙体对地基不均匀沉降反映非常敏感，设计中如果对地基不均匀沉降估计不足，易在墙体中产生阶梯形裂缝及底层窗台墙体的竖向裂缝。
（2）在檐口处没有保温措施，导致顶层横墙产生阶梯形裂缝。
（3）随意选择屋面保温材料而不考虑减少温差的作用，也会导致裂缝的产生。
（4）在混凝土柱与混凝土多孔砖和小型空心砌块的相接处，缺乏相应的控制裂缝措施，也会导致裂缝的产生。
3.施工方面
施工时砌筑操作不规范，没有按照《混凝土多孔砖建筑技术规程》进行施工，没有按照《砌体工程施工质量验收规范》（GB50203）和根据混凝土多孔砖的特性进行施工质量控制。
（1）砌筑时砖块的组砌方法不准确或铺浆不饱满。
（2）砌筑砂浆的稠度较大或混凝土多孔砖含水率较高，砌筑施工时发生了游砖。
（3）墙面粉刷时没有清除墙面浮灰，没有涂刷界面剂或涂刷纯水泥浆，造成粉刷层脱壳开裂。
（4）粉刷层过厚，造成粉刷层因自重开裂或空鼓开裂。
（5）砌筑施工时每日的砌筑高度过高，砌体在砖自重作用下砂浆灰缝压缩下沉，从而引起墙体的裂缝。
（6）砖墙没有按规定设置构造柱，墙体长度过长而产生收缩裂缝。
（7）砌体施工时，墙柱、墙粱以及门窗洞口边等关键部位的施工方法不准确，在墙柱间因墙体结构收缩时没有可靠拉接而产生裂缝、在墙粱间因墙体下沉而产生裂缝、门窗洞口因没有实砌砖块而安装不牢门窗的问题。
（8）砖墙转角处和纵横墙交接处等复杂受力处的墙体没有同时砌筑，或没有设置构造柱，造成砌体在砌筑时就产生了施工间断的间隙缝。
（9）粉刷层强度远高于砌体强度，在粉刷层和砌体间的界面应力下，引起粉刷层龟裂。
三、墙体裂缝防治措施
1.材料方面
（1）混凝土多孔砖、小型空心砌块产品质量应符合JC 943-2004《混凝土多孔砖》、GB 8239《普通混凝土小型空心砌块》及GB/T15229《轻集料混凝土小型空心砌块》标准的规定，其抗冻性指标必须符合国家标准的相关规定。施工时所用产品的龄期必须超过28d。产品应有产品出厂合格证和检验报告，进场后还应进行抽样复检。复检的项目应包括尺寸偏差、外观质量和强度等级等，必须先符合设计要求。
（2）混凝土多孔砖和小型空心砌块墙体应采用粘结性好、保水性好的专用砂浆砌筑，其技术性能指标应符合JC 860《混凝土小型空心砌块和混凝土砖砌筑砂浆》标准的规定，强度等级必须符合设计要求。
2.设计方面
（1）混凝土多孔砖、小型空心砌块墙体应设伸缩缝，间距不宜大于40m。
（2）防治顶层墙体裂缝的关键是降低屋面与墙体之间的温度差。因此必须同时设保温层，在檐口处的保温层应满铺，不得出现空档。在屋盖适当部位应设置分隔缝。
（3）混凝土多孔砖、小型空心砌块墙体内外墙交接处和纵横墙交接处，应沿高度每600mm设拉结钢筋，其中在顶层、底层、门窗洞口上下，拉结钢筋宜适当加密。
（4）混凝土多孔砖、小型空心砌块墙体与后砌填充墙，应沿高度每600mm设置拉结钢筋网片。
（5）提高顶层混凝土多孔砖和小型空心砌块及砌筑砂浆的强度等级，增强顶层墙体的抗拉、抗剪强度。
（6）在各层窗台处均设置钢筋混凝土窗台梁，以减少由于压力差引起的裂缝，同时提高底层窗台下砌筑砂浆的强度等级。
（7）有可能产生基础不均匀沉降的工程，可适当增加基础圈梁的刚度，以控制裂缝的产生。
3.施工方面
（1）砌筑工人应持证上岗，无上岗证者不得上岗。上岗前应做好技术交底，要求每一层的同部位墙体应由同一人施工。
（2）墙体所使用混凝土多孔砖、小型空心砌块的生产厂家必须具有准用证。砌筑前，应将混凝土多孔砖和小型空心砌块表面的污物清除，不得使用未到28d龄期或潮湿的混凝土多孔砖和小型空心砌块进行砌筑。断裂的混凝土多孔砖和小型空心砌块不得使用。
（3）砌筑水平灰缝时用座浆法铺浆，砌筑竖缝时先将混凝土多孔砖和小型空心砌块端面朝上铺满砂浆，然后上墙挤坚，并用瓦刀在竖缝中插捣密实，做到随砌随勾缝，以保证墙体有足够的抗拉、抗剪强度。若需要移动已砌好的砌体或被撞动的混凝土多孔砖和小型空心砌块，应重新铺浆砌筑。
（4）配制砂浆的原材料必须符合要求，设计配合比应有良好的和易性，砂浆稠度宜控制在50mm-70mm，施工配合比必须准确，保证砂浆强度达到设计要求。
（5）顶层的内粉刷应在屋面施工完毕后进行，以降低温差的影响。内、外墙的粉刷宜在砌体工程完工，并在墙体干缩基本稳定后施工，以防止粉刷开裂。
四、结束语
在建筑工程中应用混凝土多孔砖这种新型墙体材料，无论是混凝土多孔砖的生产单位、还是使用混凝土多孔砖的建筑施工单位混凝土多孔砖都必须抓好混凝土多孔砖生产和施工的各个环节的质量控制。通过对混凝土多孔砖的生产工艺过程和施工现场的严格管理，并在结构设计时采取综合性预防措施，就能够达到预防和减少混凝土多孔砖墙体产生裂缝的目的。
参考文献：
[1]刘立新,田高燕等.混凝土多孔砖干燥收缩性能研究[J].新型建筑材料.2008.
[2]王书祥,任泉昌.混凝土多孔砖砌体力学性能试验研究.[J]新型建筑材料.2006.