The phase structure and hydrogen storage properties of LaMg 3.70 Ni 1.18 alloy were investigated. The LaMg 3.70 Ni 1.18 alloy consists of main LaMg 2 Ni phase, minor La 2 Mg 17 and LaMg 3 phases. The alloy can be activated in the first hydriding/dehydriding process, and initial LaMg 2 Ni, La 2 Mg 17 , and LaMg 3 phases transfer to LaH 2.34 , Mg, and Mg 2 Ni phases after activation. The reversible hydrogen storage capacity of the LaMg 3.70 Ni 1.18 alloy is 2.47 wt.% at 558 K, which is higher than that of the LaMg 2 Ni alloy. The pressure-composition-temperature (PCT) curves display two hydriding plateaus, corresponding to the formation of MgH 2 and Mg 2 NiH 4 . However, only one dehydriding plateau is observed, owing to the synergetic effect of hydrogen desorption between MgH 2 and Mg 2 NiH 4 . The uptake time for hydrogen content to reach 99% of saturated state is less than 250 s, and 90% hydrogen can be released in 1200 s in the experimental conditions, showing fast kinetics in hydriding and dehydriding. The activation energies of the LaMg 3.70 Ni 1.18 alloy are -51.5 ± 1.1 kJ/mol and -57.0 ± 0.6 kJ/mol for hydriding and dehydriding, respectively. The hydriding/dehydriding kinetics of the LaMg 3.70 Ni 1.18 alloy is better than that of the Mg 2 Ni alloy, owing to the lower activation energy values.
The phase structure and hydrogen storage properties of LaMg 3.70 Ni 1.18 alloy were investigated. The LaMg 3.70 Ni 1.18 alloy consists of main LaMg 2 Ni phase, minor La 2 Mg 17 and LaMg 3 phases. The alloy can be activated in the first hydriding / dehydriding process, and initial LaMg 2 Ni, La 2 Mg 17, and LaMg 3 phases transfer to LaH 2.34, Mg, and Mg 2 Ni phases after activation. The reversible hydrogen storage capacity of the LaMg 3.70 Ni 1.18 alloy is 2.47 wt.% at 558 K, which is higher than that of the LaMg 2 Ni alloy. The pressure-composition-temperature (PCT) curves display two hydriding plateaus, corresponding to the formation of MgH 2 and Mg 2 NiH 4. However, only one dehydriding plateau is observed, owing to the synergetic effect of hydrogen desorption between MgH 2 and Mg 2 NiH 4. The uptake time for hydrogen content to reach 99% of saturated state is less than 250 s, and 90% hydrogen can be released in 1200 s in the experimental conditions, showing fast kinetics in hydrid ing and dehydriding. The activation energies of the LaMg 3.70 Ni 1.18 alloy are -51.5 ± 1.1 kJ / mol and -57.0 ± 0.6 kJ / mol for hydriding and dehydriding, respectively. The hydriding / dehydriding kinetics of the LaMg 3.70 Ni 1.18 alloy is better than that of the Mg 2 Ni alloy, owing to the lower activation energy values.