The microstructures and damping property of supersaturated ZnA127Ce alloy during natural aging have been investigated. H-800 TEM was mainly used to research the microstructures. The relationship between microstructure and damping property was primarily studied. The results showed that solution plus natural aging was the best heat treatment, which could improve the damping property. Both continuous precipitation and cellular reaction occurred during the aging. Continuous precipitation follows the sequence: β→spherical GP zones→elliptical GP zones→intermediate phase R→n. The cellular reaction can be written as follows:β→a+n+ε.
The microstructures and damping property of supersaturated ZnA127Ce alloy during natural aging have been investigated. H-800 TEM was mainly used to research the microstructures. The relationship between microstructure and damping property was primarily studied. The results showed that solution plus natural aging was the best heat treatment, which could improve the damping property. Both continuous precipitation and cellular reaction occurred during the aging. Continuous reaction follows the sequence: β → spherical GP zones → elliptical GP zones → intermediate phase R → n. The cellular reaction can be written as follows: β → a + n + ε.