The effect of alloying elements V and Al on microstructure and room temperature fracture toughness of an experimental Nb-Si in-situ composite was investigated. The Nb-Si alloys with different amount of V and Al were prepared by non-consumable arc-melting furnace. The experimental results showed that with the addition of V and Al, the microstructure of the Nb-Si materials transformed from Nbss+Nb3Si to Nbss+Nb5Si3 and the lattice parameters of Nbss phase decreased, and the alloying element V promoted the formation of the finer Nbss structure. It was observed that the room temperature fracture toughness was improved by the addition of V and Al, and the optimum room-temperature fracture toughness of the material appeared in the alloy with 2.6at.%V and 3.6at.%Al. The improvement of room temperature fracture toughness may be mainly attributed to the increment of the volume fraction of Nbss phase and the decrement of the silicide phase size.
The effect of alloying elements V and Al on microstructure and room temperature fracture toughness of an experimental Nb-Si in-situ composite was investigated. The Nb-Si alloys with different amount of V and Al were prepared by non-consumable arc-melting furnace . The experimental results showed that with the addition of V and Al, the microstructure of the Nb-Si materials transformed from Nbss + Nb3Si to Nbss + Nb5Si3 and the lattice parameters of Nbss phase decreased, and the alloying element V promoted the formation of the finer Nbss structure. It was observed that the room temperature fracture toughness was improved by the addition of V and Al, and the optimum room-temperature fracture toughness of the material appeared in the alloy with 2.6 at.% V and 3.6 at.% Al . The improvement of room temperature fracture toughness may be mainly attributed to the increment of the volume fraction of Nbss phase and the decrement of the silicide phase size.