本文对砂浆中埋置钢筋的试件进行了快速锈蚀试验研究。根据试验结果 ,环境温度对由于Cl- 引起的钢筋锈蚀的锈蚀率有重要的影响。在 4 0℃以下 ,增加环境温度显著增加锈蚀率 ,在 4 0℃以上增加温度 ,锈蚀率反而下降。本文对可能的原因进行了分析
In this paper, rapid corrosion test was carried out on the specimens embedded in mortar. According to the test results, the ambient temperature has a significant effect on the corrosion rate of steel due to Cl-induced corrosion. Below 4 0 ℃, increasing the ambient temperature significantly increased the corrosion rate, increasing the temperature above 40 ℃, the corrosion rate but decreased. This article analyzes the possible causes