The effect of Sm-rich liquid phase(Sm2Co3) on magnetic properties and microstructure of 2:17-type Sm-Co magnet was studied.Three phases existed in liquid phase ingot,and took on white,dark grey and grey,respectively.It was found that the composition of the greyarea was similar to the nominal one.Our results indicated that the optimal composition was obtained at 3 wt.% liquid phase added,and themagnetic properties were Br=11.58 kGs,Hci>26 kOe,(BH)m=29.51 MGOe.Br increased by 3%,Hci was 13 times larger,and(BH)m was 6times bigger than none liquid phase magnets.Moreover,with the aging time decreasing from 20 to 8 h,the squareness of the demagnetizationcurves got better,while the coercivity of the samples decreased.It revealed that Sm(Co,Cu)5 phase also precipitated at particle boundaries.Itmaybe also enhanced the coercivity.
The effect of Sm-rich liquid phase (Sm2Co3) on magnetic properties and microstructure of 2: 17-type Sm-Co magnet was studied. Three phases existed in liquid phase ingot, and took on white, dark gray and gray, respectively. It was found that the composition of the gray matter was similar to the nominal one. Our results indicated that the optimal composition was obtained at 3 wt.% liquid phase added, and the magnetic properties were Br = 11.58 kGs, Hci> 26 kOe, (BH) m = 29.51 MGOe.Br increased by 3%, Hci was 13 times larger, and (BH) m was 6 times bigger than none liquid phase magnets.Moreover, with the aging time decreasing from 20 to 8 h, the squareness of the demagnetizationcurves got better, while the coercivity of the samples decreased. Titrated that Sm (Co, Cu) 5 phase also precipitated at particle boundaries. Itmaybe also enhanced the coercivity.