苏钢R6mROKOP连铸机于1995年3月25日热试一次成功,该铸机为二机二流罗可普全弧形方坯连铸机,铸机半径为R6m,流间距为1200mm,视铸坯断面不同拉速范围为0.3～3.3m/min,定尺范围2.6～6m,连铸断面为120×120mm~2,135×135mm~2,150×l50mm~2,160×220mm~2共四种规格,设计年产量为10～12万吨/年。采用一座10t转炉冶炼钢水来配合连铸生产,铸机单炉浇铸时间与转炉冶炼周期一致,均定为30min,单炉出钢 Suyou Steel R6mROKOP continuous casting machine was successfully tested on March 25, 1995. The casting machine is a two-machine two-flow Roque all-arc billet continuous casting machine with a radius of R6m and a flow spacing of 1200mm, The different pulling speed range of billet section is 0.3 ~ 3.3m / min, the range of fixed length is 2.6 ~ 6m, the continuous casting section is 120 × 120mm ~ 2,135 × 135mm ~ 2,150 × l50mm ~ 2,160 × 220mm ~ 2, the designed annual output For 10 to 120,000 tons / year. A 10t converter smelting molten steel to match the continuous casting production, casting machine casting time consistent with the furnace smelting cycle, are set at 30min, a single tapping