【摘 要】
：
Semisolid metal forming by a novel sloping plate process was studied. A sloping plate with wavelike surface was used to prepare semisolid alloy. Semisolid bille
【机 构】
：
College of Materials and Metallurgy
论文部分内容阅读
Semisolid metal forming by a novel sloping plate process was studied. A sloping plate with wavelike surface was used to prepare semisolid alloy. Semisolid billets and slurries with good microstructures and excellent property were prepared by cooling or preheating the sloping plate. During preparing semisolid alloy by the proposed process, the co-action of burst nucleation and dendrite fragmentation causes fine spherical microstructure formation, and casting temperature, cooling strength and sloping angle are the main factors influencing the alloy microstructure. Under the current experimental conditions, in order to prepare good quality semisolid billets, proper casting temperature ranges of 660-690 ℃ for AlMg3 alloy and 660-680 ℃ for AlSi6Mg2 alloy are suggested. A small car hub wheel of AlSi6Mg2 alloy was thixoformed, and its pattern and inner microstructure are fine. The reasonable technological conditions for preparing AlSi6Mg2 slurry are also proposed: the sloping plate preheating temperature is 300 ℃, and the casting temperature is 680 ℃.
其他文献
Using embedded-atom-method potential for Pd and MORSE potential for the interaction between H and Pd atoms,the adsorption properties of H atoms on Pd (211),(311
The highly pure nano-crystal Mg,Al-hydrotalcite with titania doping was synthesized by one-step liquid reaction method at atmospheric pressure. The preparation
Solvothermal technique, an one-step soft solution-processing route was successfully employed to synthesize single crystalline CdS nanowires in ethylenediamine m
The effect of cooling rate on the solidification process of Al-2.06%Si-1.58%Mg was numerically and experimentally investigated. The solidification paths and the
The aluminium tubes with high strength and smooth outer-surface can be produced by non-mandrel drawing process. It is an effective method to study forming mecha
Electrical conductivities of micron-scale aluminum wires were quantitatively measured by a four-point atomic force microscope (AFM) probe. This technique is a c
BiFeO3 (BFO) thin films were prepared on Pt(111)/TiO2/SiO2/Si(100) substrates by the pulsed-laser deposition (PLD) technique at a low temperature of 450℃. The
Cu47Ti34Zr11Ni8,(Cu47Ti34Zr11Ni8)99Si and (Cu47Ti34Zr11Ni8)99Al bulk metallic glass were prepared by copper mold casting method,and the thermal stability,mechan
Hydroxyapatite/titania (HA/TiO2) double layers were coated onto Ti scaffolds throughout for orthopaedic applications by sol-gel method. Differential scanning ca
Cu-Sn-Zn ternary alloy layer with 10 μm thickness was prepared through electroless plating method. The influences of process conditions including the concentra