Micro parts are more difficult to be formed than macro parts because of size effects. The size effects on the flow stress of copper alloy C3602 with different lubricants were studied. Specimens were heat treated at 350℃ for 1 h and 700℃ for 3 h in nitrogen atmosphere, respectively.The initial diameters of the specimens were varied from 5 to 1 mm with a height-to-diameter ratio h0/D0 = 1.5. Cylinder compression was carried out in the lubrication condition with talc powder, without lubricant, with petroleum jelly, and with vegetable oil. The experiment was carded out at room temperature on a universal testing machine INSTRON 5569 with a strain rate of ε= 0.0025/s. The results show that with the same lubricant, the yield strength decreases with a decrease in specimen size for the specimens annealed at 350℃ for 1 h; however, it in-creases with a decrease in specimen size for the specimens annealed at 700℃ for 3 h. The yield strength decreases with an increase in grain size. The influences of lubricants on yield strength become larger with miniaturization of the specimens.