In the present study, closed-cell aluminum foams with different percentages of erbium(Er) element were successfully prepared. The distribution and existence form of erbium(Er) element and its effect on the compressive properties of the foams were investigated. Results show that Er uniformly distributes in the cell walls in the forms of Al3 Er intermetallic compound and Al-Er solid solutions. Compared with commercially pure aluminum foam, Er-containing foams possess higher micro-hardness, compressive strength and energy absorption capacity due to solid solution strengthening and second phase strengthening effects. Additionally, the amount of Er element should be controlled in the range of 0.10 wt.%-0.50 wt.% in order to obtain a good combination of compressive strength and energy absorption properties. In the present study, closed-cell aluminum foams with different percentages of erbium (Er) element were successfully prepared. The distribution and existence of erbium (Er) element and its effect on the compressive properties of the foams were investigated. Eriform distributes in the cell walls in the forms of Al3 Er intermetallic compound and Al-Er solid solutions. Compared with commercially pure aluminum foam, Er-containing foams possess higher micro-hardness, compressive strength and energy absorption capacity due to solid solution strengthening and second phase strengthening effects. Additionally, the amount of Er element should be controlled in the range of 0.10 wt.% - 0.50 wt.% in order to obtain a good combination of compressive strength and energy absorption properties.