【摘 要】
：
The influences of RE-modification and Sr-modification on the hydrogen content and surface oxide film of A356 aluminum alloy melt were investigated. The hydrogen
【机 构】
：
School of Material Science and Engineering
论文部分内容阅读
The influences of RE-modification and Sr-modification on the hydrogen content and surface oxide film of A356 aluminum alloy melt were investigated. The hydrogen content of the melt was measured by reduce pressure test. The phases in the surface oxide film were analyzed by X-ray diffractometry (XRD), and the morphology of the surface oxide film was observed by scanning electronic microscopy (SEM). The results show that RE-modification reduces the hydrogen content of A356 aluminum alloy greatly.Contrarily, Sr-modification increases the hydrogen content remarkably. After being treated with RE, a large number of LaAl11O18 consisting of Al2O3 and La2O3, are generated in the surface oxide film of A356 alloy. The surface oxide film of Sr-modification is almost composed of Al2SrO4. According to the results of SEM, the surface oxide film of Sr-modification is very easy to crack,destroy the continuity and compactness of surface oxide film, accelerate the vapor diffusing into the melt, consequently, increase the hydrogen content of A356 alloy melt significantly. But RE-modification makes the surface oxide film compact, and restrains the aluminum exposed to water, so reduces the hydrogen content of A356 alloy melt.
其他文献
Eu3+ doped SiO2 nano-crystalline glasses were prepared by sol-gel method. The broad peak of XRD pattern indicates an amorphous SiO2 matrix. The affection of ann
Long lasting phosphorescence (LLP) was observed in Eu2+, Ce3+ co-doped strontium borate glasses prepared under the reducing atmosphere due to the emission of bo
Phase formation in ternary system of complex Sc, Na and Li phosphates was studied at 950 ℃ and synthesis of new phases of definite composition was carried out.
Er3+/Yb3+-codoped oxyfluoride crystallite glass was prepared with melting technique. The compositions and the melting temperature and the annealing temperature
Based on crystal plasticity theory and surface layer model, relation of flow stress to billet dimension and grain size was built,and rationality of derived rela
The structure defects such as stray grains during unidirectional solidification can severely reduce the performance of single crystal turbine blades. A dendrite
To carry out biaxial tensile test in sheet metal, the biaxial tensile testing system was established. True stress-true strain curves of three kinds of aluminum
The (100)-orientated diamond film was deposited by hot-filament chemical vapor deposition (HFCVD) technology with a positive DC bias voltage. The morphology,X-r
The oxidation behavior of NiTi and NiTiNb alloys containing different amounts of Nb (7%, 9%, mole fraction) were studied at 800 ℃ in air. It is found that the
The tool flank begins to wear out as soon as cutting process proceeds. Cutting parameters such as cutting forces and cutting temperature will vary with increasi