The synthesis, properties and dispersion mechanism of sulphonated acetone-formaldehyde superplasticizer(SAF) were presented. This superplasticizer was synthesized by the reaction among acetone, formaldehyde, sodium sulfite and pyrosulfite. The structure and property were respectively characterized by IR and surface tension measurement. Performance of SAF in cement was evaluated by paste flow as well as heat calorimetry. The dispersion mechanism was identified via adsorption and zeta potential measurement. The results show that cement paste mixed with SAF shows good fluidity. SAF exerts little retarding effect on cement paste and it behaves like a typical polycondensate superplasticizer. The main dispersion mechanism of SAF is attributed to electrostatic repulsion.
The synthesis, properties and dispersion mechanism of sulphonated acetone-formaldehyde superplasticizer (SAF) were presented. This superplasticizer was synthesized by the reaction among acetone, formaldehyde, sodium sulfite and pyrosulfite. The structure and properties were separately by IR and surface tension measurement. Performance of SAF in cement was evaluated by paste flow as well as heat calorimetry. The dispersion mechanism was identified via adsorption and zeta potential measurement. The results show that cement paste mixed with SAF shows good fluidity. SAF exerts little retarding effect on cement paste and it behaves like a typical polycondensate superplasticizer. The main dispersion mechanism of SAF is attributed to electrostatic repulsion.