The in situ Al 2O 3p TiC p/Al composite was fabricated by XD (exothermic dispersion) process in TiO 2 Al C system, and the effect of carbon content on the microstructure of the fabricated composite and the reactive temperature characteristics had been studied. The results show that carbon content affects the microstructure and reactive temperature of Al 2O 3p TiC p/Al composite greatly. The quantity of TiC phases in the fabricated composites increases, while the Al 3Ti phases reduces with increasing carbon content. And when C/TiO 2 molecular ratio is equal to one, the Al 3Ti phase nearly disappears. High temperature metallurgical field caused by strong exothermic reaction influences the synthetic reaction greatly, and higher synthetic temperature was favorable to the synthesis of Al 2O 3p TiC p reinforce particles.
The in situ Al 2 O 3p TiC p / Al composite was fabricated by XD (exothermic dispersion) process in TiO 2 Al C system, and the effect of carbon content on the microstructure of the fabricated composite and the reactive temperature characteristics had been studied. results show that carbon content affects the microstructure and reactive temperature of Al 2O 3p TiC p / Al composite greatly. The quantity of TiC phases in the fabricated composites increases, while the Al 3Ti phases reduces with increasing carbon content. And when C / TiO 2 Molecular ratio is equal to one, the Al 3Ti phase are disappears. High temperature metallurgical field caused by strong exothermic reaction influences the synthetic reaction greatly, and higher synthetic temperature was favorable to the synthesis of Al 2O 3p TiC p reinforce particles.