Yellowish nitrogen-doped titania was produced through sol-gel method in mild condition, with the elemental ni- trogen derived from aqua ammonia. The titania catalysts were characterized using XRD, BET, TEM, XPS, and UV-Vis diffuse reflectance spectrophotometer, and their photocatalytic activities were evaluated under UV and visible light, respec- tively. The XRD results showed that all titania catalysts were anatase. More significantly, the crystallite size of nitro- gen-doped titania increased with an increase in N/Ti proportion, and the doping of nitrogen could extend the absorption shoulder into the visible-light region, thus it possessed a higher visible-light activity illustrated by decolorization of methyl orange (65.3%) under the irradiation of visible light, whereas pure titania showed little of such kind of visible light activity. The UV-light activity of nitrogen-doped titania catalysts was worse than that of pure titania and Degussa P25. In the range of N/Ti proportion of 4-10 mol%, the activity of nitrogen-doped titania weakened appreciably in the visible-light region as the N/Ti proportion increased, whereas a reverse relationship existed under the irradiation of UV light. Yellowish nitrogen-doped titania was produced through sol-gel method in mild condition with the elemental dihydrogen derived from aqua ammonia. The titania catalysts were characterized using XRD, BET, TEM, XPS, and UV-Vis diffuse reflectance spectrophotometer, and The photocatalytic activities were evaluated under UV and visible light, respecively. The XRD results showed that all titania catalysts were anatase. More significantly, the crystallite size of nitro- gen-doped titania increased with an increase in N / Ti proportion, and the doping of nitrogen could extend the absorption shoulder into the visible-light region, thus it possessed a higher visible-light activity illustrated by decolorization of methyl orange (65.3%) under the irradiation of visible light, yet pure titania showed little of such kind of visible light activity. The UV-light activity of nitrogen-doped titania catalysts was worse than that of pure titania and Degussa P25. In the range of N / Ti proport of 4- The activity of nitrogen-doped titania weakened appreciably in the visible-light region as the N / Ti proportion increased, a reverse relationship existed under the irradiation of UV light.