【摘 要】
：
三元共聚尼龙/SAN/NBR(50/25/25质量比)共混物在酚醛树脂的作用下进行动态硫化。当硫化剂用量大于8份质量份,下同时可制得具有均衡力学性能特别是超高韧性的共混合金。
【机 构】
：
上海交通大学高分子材料研究所,上海交通大学高分子材料研究所,上海交通大学高分子材料研究所 上海200240,上海200240,上海200240
论文部分内容阅读
三元共聚尼龙/SAN/NBR(50/25/25质量比)共混物在酚醛树脂的作用下进行动态硫化。当硫化剂用量大于8份质量份,下同时可制得具有均衡力学性能特别是超高韧性的共混合金。用扫描电镜对在液氮中淬断并用四氢呋喃刻蚀的分别含0,4,8,10份酚醛树脂的试样进行分析,发现分散相粒径随硫化剂用量的增加而减小,粒径分布变得更加均匀。
The terpolymer nylon / SAN / NBR (50/25/25 mass ratio) blends were dynamically vulcanized under phenolic resin. When the amount of curing agent is greater than 8 parts by mass, the same time under the same system can be prepared with balanced mechanical properties, especially high toughness of the blended alloy. Scanning electron microscopy analysis of samples containing 0, 4, 8 and 10 parts of phenolic resin, which were quenched in liquid nitrogen and digested with tetrahydrofuran, respectively, showed that the particle size of disperse phase decreased with the increase of the amount of vulcanizing agent. Distribution becomes more uniform.
其他文献
目的 研究尿激酶型纤溶酶原激活剂（uPA）及受体（uPAR）在髓母细胞瘤中的表达及临床意义。方法 应用免疫组化LSAB法检测50例髓母细胞瘤中uPA及uPAR的表达,结合临床随访,使用Cox回归
水冷式发动机冷却系零部件受热面温度随水垢增厚而升高,将导致过热。为保证发动机正常运转,必须减少冷却系水垢的厚度。
Water-cooled engine cooling system components he
帝斯曼公司旗下从事投资的业务部帝斯曼投资公司于2008年3月6日宣布,参与中国从事生物塑料业务的天津绿色生物科学公司2000万美元(1300万欧元)的联合投资。这项投资将用于在
二、检验夹具的结构(二)检验夹具的下部结构1.平台平台式检验夹具主要用于 A 级夹具或制件既长又大的场合,见图2.25。平台结构有二种型式(1)用铸铁铸成一体,见图2.26和
Sec
会计模拟实验是指“以一个会计主体在一定时期内发生的实际经济业务以及产生和形成这些经济业务相关的内部和外部经济联系、会计核算程序、会计凭证在各会计岗位间的传递程序
齐河段的工人同志们,在锥探工作中创造了运用十公尺大锥的三角竹管架。这一办法能使大锥一次锥到底,不再换锥,而且锥杆不跑锥,不仅保证了质量,而且提高效率百分之二十八点五
在汽车前轴的疲劳寿命试验中,若忽略了惯性力,或估计的偏差较大,则会造成较大的加载误差,对试验结果的影响甚大。为此,本文采用三种方法测试和计算惯性力,并进行了分析、对比
我科于1994年1月至1996年6月按1987年成都会议制定的标准,共收治小儿反复下呼吸道感染58例,随机分为治疗组38例与对照组20例,两组年龄和性别分布无差异(P>0.05),病情轻重比
儿童系统性红斑狼疮较少见,临床上易误诊。我院自1989～1996年11月共收治14例,分析如下。 1 临床资料 1.1 一般资料:14例均系住院患儿,诊断标准按1982年风湿病学的系统性红斑
转化生长因子 β1(TGF β1)是人体多种组织细胞的生长调控因子 ,其对大多数正常细胞及上皮性肿瘤细胞具有生长抑制作用。转化生长因子 β1Ⅱ 型受体 (TβRⅡ)的表达减少是机