【摘 要】
：
研究了不同硫化体系和不同硫化剂用量的天然橡胶与甲基硅油的相容性.结果表明,硫黄硫化胶与甲基硅油具有较好相容性,其中半有效硫化体系硫化胶在85℃硅油中浸泡168h后力学性
【机 构】
：
北京航空材料研究院;海军驻北京地区航空军事代表室
论文部分内容阅读
研究了不同硫化体系和不同硫化剂用量的天然橡胶与甲基硅油的相容性.结果表明,硫黄硫化胶与甲基硅油具有较好相容性,其中半有效硫化体系硫化胶在85℃硅油中浸泡168h后力学性能最好,拉伸强度仍高达17.8MPa,质量变化率只有1.41%,基本不溶胀.“,”The compatibility between methyl silicone oil and natural rubber with different vulcanization systems and different amount of curing agent were investigated.The results showed that the compatibility between natural rubber vulcanizate vulcanized by sulfur vulcanization system and methyl silicone oil was good,and the mechanical properties of the vulcanizate vulcanized by semi-efficient vulcanization system were the best after immersion in the silicone oil at 85℃ for 168h,and the tensile strength was still up to 17.8 MPa,and the mass changing was only 1.41%,and the swelling had not almost occurred.
其他文献
通过力学性能测试和橡胶加工分析仪(RPA2000)等方法研究了硫化体系和补强体系对AFLAS100S橡胶性能的影响.结果表明,交联剂BIBP用量为1.8份,交联助剂TAIC为7份,炭黑N990/炭黑N
工程实践中逐渐变得不可忽视的样本个性问题提出了有关材料特性的新的研究要求：实际的材料在很小的尺度上由具有不同特性的成分构成，从而在那个尺度下形成难以观测，但却对破坏过
据中国橡胶信息网消息,菲律宾政府今后将对胶农提供财政、基础设施和种植技术等方面的支持,以使该国天然橡胶产量在未来10年年均增长3.7%.据了解,菲律宾天然橡胶产量仅占全
在三相同轴柱壳剪切滞后模型的基础上，分析含有界面层的碳纳米管复合材料粘弹性应力、位移和模量等的频率响应。在交变外载下代表性体积单元中应力和位移频率响应的相位滞后偏
蜂窝夹芯结构具有较高的比强度、比刚度和优良的隔热隔振性能，被广泛应用于航空航天结构件中。蜂窝夹芯结构也是高超音速飞行器金属热防护系统面板的理想候选材料，其正交各向异
本文对缝纫造成的局部细观结构进行了试验研究，引入了四个结构参数进行描述，井对各参数进行定最的测簧。发展了纤维弯曲模型，得到纤维偏转角和体积含量的空间非均匀分布，使人们对
保持CR硫化体系不变,以NBR硫化体系为变量,研究了普通硫黄硫化体系、有效硫化体系(硫载体)、半有效硫化体系、高促低硫硫化体系、过氧化物硫化体系及TCY硫化体系对NBR/CR共混
传统烧烤,由于烟熏火燎,烟雾缭绕的不卫生,一直登不了大雅之堂。但是人们对于烧烤的热情,从来没有因此而减退过。陶瓷烧烤,它采用耐高温的陶瓷材料作为烤盘,对各种食物进行烧
本文以现有的试验研究成果为分析基础，应用ANSYS有限元软件，考虑混凝土材料的非线性，对两根非预应力FRP筋混凝土梁和两根预应力FRP筋混凝十梁受力过程进行模拟分析。详细讨论了
NMC脊柱疾病中的一种临床表现，在腰椎疾病中出现的NMC是由于马尾神经缺血受损引起的马尾源性神经性间歇性跋行(cauda equina- IC)，在颈、胸椎疾病时出现的NMC是由于脊髓缺血受