【摘 要】
：
各类箱式电炉、井式渗碳炉中的电阻丝引出棒都是用一段不锈钢棒焊在电阻丝的末端,因引出棒有一段在炉中,长期工作后会造成焊接部分氧化,电阻过大而被烧断。我们做了如下改进
论文部分内容阅读
各类箱式电炉、井式渗碳炉中的电阻丝引出棒都是用一段不锈钢棒焊在电阻丝的末端,因引出棒有一段在炉中,长期工作后会造成焊接部分氧化,电阻过大而被烧断。我们做了如下改进,解决了上述问题,使用三年(连续生产不停炉)一直很正常。具体方法如下,将一段φ12毫米的普通钢管两头锻成圆头(见图),中间留一孔(约φ5.5毫米)将护
All kinds of box-type electric furnace, pit-type carburizing furnace resistance wire leads are using a stainless steel rod welded wire resistance at the end of the lead rod has a period in the furnace, long-term work will cause the welding part of the oxidation resistance Big and was burned. We made the following improvements to solve the above problems, the use of three years (continuous production without stop) has been normal. The specific method is as follows, a section of φ12 mm ordinary steel forged into two round head (see photo), leaving a hole in the middle (about φ5.5 mm) will protect
其他文献
弹体冲压毛坯收口前结构尺寸的设计计算,在有关教材和工厂实际生产中一直沿用逐点按“等面积法”进行计算,但实际收口过程中金属塑性变形大部与“等面积法”假设条件是不相符
3Cr2W8V钢具有高温回火脆性,断裂韧性的谷值与二次硬化峰相对应,冲击韧性的谷值较二次硬化峰高出50～100℃。淬火温度自1200℃以上,经650℃以上回火后,断裂方式由穿晶转为沿晶,
蠕铁作为一种新型工程材料问世以来,日益受到人们的重视。人们先后研制出了各种各样的蠕化剂和蠕化方法。如何选择应用,是摆在蠕铁生产者特别是试生产者面前的重要问题之一
合金钢经过调质其硬度达到HB 300～400(HRC 32～43)后,基体中大量弥散分布着坚硬的合金渗碳体,因而使得在切削加工时,加快刀具的磨损,降低刀具的寿命,所以,如何提高高速钢刀具的
本文对切割大厚度工件过程中所出现的某些特殊问题进行了概略的分析,对实现大厚度工件的切割加工指出了有效的工艺措施。电火花线切割加工超过100毫米的工件,例如200毫米乃
钢在相变过程的超塑性效应,虽已发现多年,但一直认为是一种异常现象,有关这方面的试验资料很少,而对其实际运用方面的探讨和总结尤为不够。直至近几年来,才受到愈益重视。随
本文用共浸法制备了一系列Pt—Sn—RE催化剂,以正庚烷为原料,研究了它们的反应性能。在不同的反应条件下稀土元素对Pt—Sn催化剂的改性作用不同。此外,Sn/Pt原子比不同对催化
为通信和军用市场提供全套MMIC基产品的Hittite Microwave公司推出甚小孔径终端(VSAT)、微波无线电通信、测试设备和传感器用的两款表面安装(SMT)GaAs MMIC混频器和一款新的S
本课题对普通话水平测试说话项目的应试情况、失误原因、失分率以及应试人应试说话自我满意度等作了详尽的调查分析,并对现行普通话培训教材与教学模式进行了反思。
This to
本文对某些高校现行教材和参考书中出现的二价金属硫化物在非氧化性酸中溶解性的计算公式及其计算结果进行了分析,认为该公式使用范围有限,不能任意推广使用,提出用另一计算