Tungsten powder was fabricated from the system CaWO4-Mg by self-propagating high-temperature synthesis (SHS) with a magnesium thermit stage. The physic-chemical change during heating and the effects of pressure of sample and diluents (W powder) on product have been studied. The experimental results show that the porosity of combustion product and the particle size of final tungsten powder decrease with increasing pressure of sample. Addition of diluents could increase the particle size of final tungsten powder. The purity of tungsten is improved by leaching in NaOH solution. The results of spectral analysis and particle size distribution of final tungsten powder show that the final Tungsten powder has a median diameter of 0.87μm,specific surface area of 1.09m2/g and purity of above 99.0%.
Tungsten powder was fabricated from the system CaWO4-Mg by self-propagating high-temperature synthesis (SHS) with a magnesium thermit stage. The physic-chemical change during heating and the effects of pressure of sample and diluents (W powder) on product have has studied. The experimental results show that the porosity of combustion product and the particle size of final tungsten powder decrease with increasing pressure of sample. Addition of diluents could increase the particle size of final tungsten powder. The purity of tungsten is improved by leaching in NaOH solution. The results of spectral analysis and particle size distribution of final tungsten powder show that the final Tungsten powder has a median diameter of 0.87 μm, a specific surface area of 1.09 m2 / g and a purity of above 99.0%.