【摘 要】
：
为了提高铸铝合金(如AЛ-5,AЛ-9),零件之机械性能,大多数都采用淬火及时效处理。但由于铸铝合金之淬火温度伸缩性很小(如AЛ-9一般规定在535±100℃; AЛ-5规定在525±10
论文部分内容阅读
为了提高铸铝合金(如AЛ-5,AЛ-9),零件之机械性能,大多数都采用淬火及时效处理。但由于铸铝合金之淬火温度伸缩性很小(如AЛ-9一般规定在535±100℃; AЛ-5规定在525±10 ℃),同时保温时间都至少数小时以至十余小时,,因而稍有不慎如炉温稍高,炉膛温度不均,仪表失真或操作者考虑不周均能造成此等铸铝件发生所谓“过烧”现象。对已过烧之零件若不会判断
In order to improve the cast aluminum alloy (such as AЛ-5, AЛ-9), the mechanical properties of parts, most of them are quenched and aging treatment. However, since the quenching temperature of cast aluminum alloy is very small (535 ± 100 ℃ for A-9 and 525 ± 10 ℃ for A-5), the holding time is at least several hours and even ten hours, Slightly inadvertent as the furnace temperature is slightly higher, uneven furnace temperature, distortion of the instrument or the operator can cause the so-called “over-burning” phenomenon. If the parts have been burned will not judge
其他文献
随着科学技术的不断发展,近几年来液体静压技术在磨床上得到愈来愈广泛的应用,如静压轴承、静压导轨、静压螺母等。根据我厂四车间改进的一种结构简单的内圆磨具,使用情况良
随着我国黄金事业的发展,在地质及地球化学寻找金矿的科研生产中需要分析大量ppb～ppm级的金样品。为了适应这种需要,近年来研究并制定了各种高灵敏度金的分析方法,迫切需要相
江苏省燕山期岩浆侵入活动极为频繁与强烈,岩体遍布全区,规模较大者达数百平方公里,小者只及数十平方米。其中由多阶段侵入作用所构成的几个复式岩体——利国复式岩体、宁镇
广西中部極广泛地分布着中、上石炭紀黄龙灰岩和馬平灰岩以及下二迭紀的栖霞灰岩和茅口灰岩。它們在構造上多形成寬闊平緩的“箱狀”及“槽狀”短軸向斜盆地,盆地內也有上二
光阴荏苒,岁月如流,一年一度的新春佳节即将来临。本刊编辑部特向广大关心、支持刊物的热心读者和作者致以亲切的节日问候。当前,我国改革开放和经济建设进入了一个新的历史
目前应用广泛的化学键合固定相,由于在其制备过程中不能将表面活性基团全部消除,残存活性基团呈现的吸附现象影响了键合相的色谱分离性能。因此对键合相表面吸附性能的研究
1961年作者到若尔盖高原进行地貌调查,发觉此高原有不少地区分布着黄土,因而收集了一些有关资料。现介绍如下:
In 1961, the author conducted a landform survey to the R
据联合国、经济合作与发展组织和国际货币基金组织及世界银行等多家国际机构预测,1993年世界经济可望出现缓慢复苏。世界经济在经过近两年的衰退之后,1993年可望出现有限增
对电感偶合等离子光源的发展及其性质进行了讨论,对于它们在化学光谱分析中的应用作了评论,还同其它等离子光源进行了比较。
The development of inductively coupled plasm
先后读到在地质学报第41卷第3—4期上发表的和地质科学院出版的李春昱等的同名论文《浙闽中生界火山沉积岩系之研究》。他们认为磨石山组火山岩地层以熔灰岩、凝灰岩为主。