The influence of Ce on solid solution and aging process of AZ91D magnesium alloy was analyzed.The results showed that the decomposition of β-Mg17Al12 phase in AZ91D magnesium alloy at 420 ℃ could be completed within 12 h,while this process in the Ce-containing alloy required more time.In subsequent aging process at 175 ℃,Ce obviously delayed the aging process of AZglD.It was inferred that the influence of Ce on process of solid solution and aging was relative to the Ce that existed in β-Mg17Al12 phase of original structure in the form of solid solution,and the interaction of the Ce and Al was an important factor to get process of solution and aging slowly.