【摘 要】
：
Al-5Ti-B and Al-5Ti-B-Gd master alloy refiners were fabricated by fluorine salt casting method. The microstructure and phase constitution of the master alloys w
【机 构】
：
School of Materials Science and Engineering,Heilongjiang University of Science and Technology,Haerbi
论文部分内容阅读
Al-5Ti-B and Al-5Ti-B-Gd master alloy refiners were fabricated by fluorine salt casting method. The microstructure and phase constitution of the master alloys were investigated by scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray diffraction (XRD). The results show that Al-Ti-B alloy refiner consists of Al3Ti phase and TiB2 phase. After Gd is introduced into the intermediate alloy, Ti2Al20Gd phase appears in the alloy, the size of Al3Ti is significantly reduced, and Ti-Al-Gd phase is found in the edge of Al3Ti phase. At the same time, some independent Ti-Al-Gd phases appear in local areas, which are Ti2Al20Gd phase determined by micro-area electron diffraction analysis. Analysis and calculation results of the high-resolution images of the Ti2Al20Gd/Al structure show that there is no other compound at the junction between the Ti2Al20Gd phase and Al, and Ti2Al20Gd phase has a great difference in atomic space with the α-Al, which cannot be directly used as heterogeneous nucleus. But, after being decomposed in the aluminum melt, the Ti2Al20Gd phase can promote the refinement effect of the refiner. In the Al-Ti-B-Gd master alloy, there are many dispersed Al3Ti particles with a size of less than 1 μm, which can promote the Al-5Ti-B refining effect.
其他文献
粉末涂料市场与许多市场一样,由于疫情的影响,短期预计会出现下降,但长期的预测是将会趋好。据市场研究公司IRL的JoséBottino估计,2020年粉末涂料的消费量将达到235万t,粉末涂料占工业涂料市场的10.7%。IRL公司研究了2020年不同工业涂料的市场,预计该市场将总体下降6%以上。下降幅度因地区而异,初步预测显示,亚太地区将逐步得到恢复,且表现将会更强劲。预计亚太地区(尤其是中国)的表现将好于其他地区,其需求量的下降接近两位数。
日前,涂料行业资深专家段质美先生收集了鲜有报道的行业前辈戴济先生的生平事迹和资料,对于重新认识中国近现代涂料工业的早期贡献者做了一些考证并撰写了此文,并提出戴济作为中国涂料业的先驱实至名归。希望本文刊出后能引起行业关注,也欢迎进行探讨,以达到行业共识。
Large-size primary MC carbides can significantly reduce the performance of M2 high-speed steel. To better control the morphology and size of primary MC carbides
This work aims to produce a high manganese steel with more refined austenite grains and better wear resistance without sacrificing the toughness and tensile properties by Mn alloying and Ti ladle treatment in comparision to ASTM A128 Gr.E1 steel (1.0C-13M
A Mn18Cr2 steel containing TiN precipitates was fabricated by vacuum induction melting.The morphology of TiN precipitates and the interface orientation relationship between TiN and γ-Fe were characterized by means of SEM,TEM and SAED,and the formation mec
The effect of a low-frequency alternating magnetic field (AMF,0 A 0 Hz,5 A 10 Hz,10 A 10 Hz,15 A 10 Hz) on the hot tearing susceptibility (HTS) of a magnesium alloy (EV31) was systematically studied using a combination of experiment and numerical simulati
K416B Ni-based superalloy with high W content has good high temperature properties and low cost, which has a great development potential. To investigate the roo
Inconel 718 alloys were fabricated by selective laser melting under different scanning speeds to investigate the change of the morphology of molten pool, direct
Seeking high-performance computing methods to solve the problem of a large amount of calculation, low calculation efficiency, and small simulation scale on the
In this work,a new(Y,Gd)H2 precipitate was identified and systematically investigated in the as-cast Mg-6Gd-3Y-0.5Zr alloy by XRD,SEM with EDS,TEM with EDS techniques and thermodynamics analysis.Results show that the as-cast alloy contains α-Mg