【摘 要】
：
The surface nanocrystalline microstructures of 7A04 aluminium alloy was obtained by means of circulation rolling plastic deformation(CRPD),the grain refinement
【机 构】
：
Department of Materials Science and Engineering
论文部分内容阅读
The surface nanocrystalline microstructures of 7A04 aluminium alloy was obtained by means of circulation rolling plastic deformation(CRPD),the grain refinement behavior and the hardness variation were examined. X-ray diffraction(XRD) and transmission electron microscopy(TEM) were applied to characterize the microstructure of the surface layer. The experimental evidences show that,after the CRPD treatment,the mean grain size in the surface layer is about 50 nm. The microhardness of the nanostructured surface layers is enhanced significantly after CRPD compared with that of the matrix,which can be attributed primarily to the grain refinement. The microhardness at the top surface can reach about HV0.05335,while the value of the matrix is HV0.05160 or so. The surface hardening effect is obtained obviously. Besides,the thermal stability of nanocrystalline layer was investigated. The results of the XRD analysis and the microhardness measurement show that the nanocrystalline layer has better thermal-stability than the matrix. And the DSC measurement shows that the synthesis of nanostructured surface layer has influence on the phase transformation of 7A04 aluminum alloy.
其他文献
A new class of electrorheological (ER) material using rare earth (RE=Y) oxide as the substrate, NaNO3-doped Y2O3 materials, were synthesized using Na2CO3 and Y(
MgO single crystal was irradiated by neutron up to a dose of 5.74×1018 cm-2. The radiation damage and its recovery were studied by means of UV-VIS and EM spect
ZnSe/SiO2 composite thin films was prepared by sol-gel method. XRD results indicate the phase structure of ZnSe particles embedded in ZnSe/SiO2 composite thin f
The lead-free piezoelectric ceramics (K0.5Na0.5)NbO3 (abbreviated as KNN) with the relative density of 97.6% were synthesized by press-less sintering owing to t
Superlattices with varying GaN well widths (2, 3, 6, 9 nm) and fixed AlGaN barrier (8 nm) with high Al-content (x=0.65) were grown. Streaky RHEED patterns indic
A new way to prepare SiC whiskers through the induction of carbon fiber was suggested. With the processing steps of opening furnace firstly and then shutting it
Significant progress was made by the CERN RD39 collaboration in the development of super radiation-hard cryogenic silicon detectors for applications in experime
The completely degradable nanocomposites comprised of poly(propylene carbonate)(PPC) and organo-modified rectorite (OREC) were prepared by direct melt intercala
AZ31B magnesium extruded slabs prepared from LFEC were rolled at fairly lower temperature at 3, 6 and 16 m/min rolling speeds into 1 mm thickness. The results i
In this paper we introduce a framework for using quality as an incentive to promote proper application level congestion control. Through integrating a joint-sou