【摘 要】
：
采用组织分析和拉伸试验,研究加入0.5%Sb对Mg-5Y-3Sm-0.8Ca(质量分数)合金组织和力学性能的影响。结果表明,加入0.5%Sb后,合金中有高熔点Mg3Sb2相生成,且晶粒尺寸得到细化。M
【机 构】
：
河南科技大学材料科学与工程学院,有色金属共性技术河南省协同创新中心,
论文部分内容阅读
采用组织分析和拉伸试验,研究加入0.5%Sb对Mg-5Y-3Sm-0.8Ca(质量分数)合金组织和力学性能的影响。结果表明,加入0.5%Sb后,合金中有高熔点Mg3Sb2相生成,且晶粒尺寸得到细化。Mg-5Y-3Sm-0.8Ca-0.5Sb合金的室温及高温力学性能得到改善,室温和300℃时的抗拉强度分别为266 MPa和208 MPa,抗拉强度稳定性优于商用耐热镁合金WE43。
The effects of adding 0.5% Sb on the microstructure and mechanical properties of Mg-5Y-3Sm-0.8Ca (mass fraction) alloy were investigated by means of tissue analysis and tensile test. The results show that after addition of 0.5% Sb, the Mg3Sb2 phase with high melting point is formed and the grain size is refined. The mechanical properties at room temperature and high temperature of Mg-5Y-3Sm-0.8Ca-0.5Sb alloy are improved. The tensile strength at room temperature and 300 ℃ are 266 MPa and 208 MPa, respectively. The tensile strength stability is better than that of commercial heat-resistant magnesium alloy WE43.
其他文献
钢丝在拉拔前经过酸洗、磷化等表面预处理时，产生的废水、废酸、废渣污染是整个生产过程的主要污染源，其中酸雾污染问题最为突出。传统的酸洗生产线采用敞开方式作业，产生大量酸
主要介绍了各类模板法制备三维有序大孔(3DOM)无机材料的研究现状,详细说明了各类模板法的优劣性及其发展应用,为深入探索和研究3DOM无机材料提供了有用的参考信息.
研究稀土钼丝的生产工艺，并测定其力学性能。稀土钼丝拉断力超过国家标准GB4182-84(φ0.18～O．12mm)规定值的34.29％～75.14％。对结果讨论认为，稀土钼丝具有高破断拉力是因为氧化物粒子
对热镀锌金属锌锅的损坏形式、损坏机制及影响其使用寿命的因素进行分析，说明：碳和硅是影响锌锅寿命的主要化学元素；组织致密、成分均匀且适当厚度的锌锅较耐腐蚀；锌锅深度与宽度
以某低热值含钒石煤配煤燃烧灰渣为研究对象,进行了直接酸浸提钒的试验研究。通过单因素条件试验,确定了浸出液固比、硫酸用量、助浸剂添加量、浸出温度、浸出时间、搅拌速度
介绍一种钢丝热镀锌工艺，解决热镀锌污染严重、生产效率低、能耗高等问题。新工艺采用超声波复合清洗、内加热陶瓷锌锅及陶瓷压辊、气体抹试等多项新技术，真正实现了钢丝高效热
综述了金属镓的主要提纯方法及其原理、常用提纯技术及其特点、国内高纯镓企业采用的生产技术路线等,并对比了各种高纯镓制备技术的优缺点,指出了高纯镓制备过程中的注意事项
盆栽桃树有较高的观赏与果品生产价值,适宜城镇楼房阳台、楼顶、庭院栽培,是城镇绿化的有效方法。1、品种选择盆栽桃树可选择当地优良品种,苗木可以采用嫁接成苗与芽接苗,也
传统的异型拉丝模具制作复杂，使用时损耗大，改用辊拉横具可节约成本，提高生产效率。采用特制水箱拉丝机，配备新型辊拉模具，辅以先进的电气控制，使拉拔力降低20％～30％，总压缩率为95.4％，运行
采用水热法在铝片基底表面成功制备了片状花簇Co3O4超疏水表面,利用X射线衍射和扫描电镜研究了前驱体及终端产物的成分结构和表面微观形貌;探讨了水热反应时间对Co3O4表面微