【摘 要】
：
以TiB2/Cu复合粉末压坯为研究对象,应用微波烧结炉对其进行烧结。探讨了微波烧结制备TiB2/Cu复合材料的几种基本的工艺因素。结果表明,在微波烧结条件下,以SiC粉末作为辅助加
【机 构】
：
南昌航空大学材料科学与工程学院,南昌大学材料科学与工程学院,
论文部分内容阅读
以TiB2/Cu复合粉末压坯为研究对象,应用微波烧结炉对其进行烧结。探讨了微波烧结制备TiB2/Cu复合材料的几种基本的工艺因素。结果表明,在微波烧结条件下,以SiC粉末作为辅助加热,可以得到较快的升温速率,并且温度易于控制;将试样放置于SiC粉末上,可以较好地进行温度测量,试样烧结外观较好;随着烧结温度和时间的增大,试样致密度有所提高。在1 000℃烧结10min得到的致密度最高。
With TiB2 / Cu composite powder compact as the research object, it was sintered in a microwave sintering furnace. Several basic process factors for preparing TiB2 / Cu composites by microwave sintering were discussed. The results show that under the conditions of microwave sintering, SiC powder as auxiliary heating, can be faster heating rate, and the temperature is easy to control; the sample placed on the SiC powder, the temperature can be better measured, the sample sintered appearance Better; with the sintering temperature and time increases, the sample density has increased. Sintering at 1 000 ℃ 10min obtained the highest density.
其他文献
采用Fluent软件分析了不同旋转喷吹参数对铝熔体净化过程流场的影响。结果表明,600r/min偏置搅拌时,熔体内部气泡分布情况最好。熔体流速和湍流强度随转速的增加而增加,随进
采用金属型低压连串铸造工艺方法生产铝合金导体,按垂直分型和水平分型两种方案进行了试验,并进行了对比分析。两种方案均为一模8件,与常规一模两件的金属型低压铸造工艺相比
等通道转角挤压工艺(ECAP)通过不同路经的多道次挤压变形,产生大的塑性变形,可以达到细化晶粒的目的,同时也是超细晶材料制备的一种有效渠道.但试样在通过转角处会产生强烈的
根据零件具体结构的特征,确定了压铸铝合金推杆的合理位置和推杆的适当数量。生产实践表明,铸件各部位受力均衡,能顺利地被推杆推出,不会发生变形,保证了铸件质量。
Accordi
随着影像成像技术的深入研究,数字减影血管造影(DSA)的图像处理水平有了很大提高.DSA图像形成需经过复杂的成像环节才能获得,如操作不当或技术问题,会丢失部分信息或产生伪影而降低影像质量.笔者通过成像方式和技术参数的调整设定,获得了满意的影像质量效果.本研究总结经下肢动脉DSA检查患者51例的影像学资料,对下肢动脉DSA检查技术进行探讨。
全世界约3.5亿人(约占全世界总人口的5%)为慢性乙型肝炎病毒携带者[1,2],其中相当一部分患者发展为肝炎后肝硬化,此类患者有特殊的病理生理,现将我院对该类患者的麻醉处理报告如下。
通过对支架压铸件的结构分析,发现其易出现型芯孔拉伤及高度尺寸胀大的现象,原因在于原模具的浇口设计不当所致.为此,针对产品的结构特点,将原来的侧浇口改为中心浇口.结果表
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
采用扫描电镜、X射线衍射仪等分析手段,研究了热处理工艺对离心铸造变质无限冷硬铸铁轧辊组织和性能的影响。结果表明,变质无限冷硬铸铁轧辊的铸态组织是贝氏体+碳化物+少量
高阻尼合金构件工作时易于操控,减少噪声,ZA合金具有高的阻尼性能,作为阻尼材料具有很好的发展前景。综述了ZA合金阻尼特性的研究进展,介绍了ZA合金的组织特点和阻尼特性的机