Hot-corrosion behaviors of nickel-base superalloy and aluminide diffusion coating have been investigated in conditions of contents of Na2SO4 and NaCl molten salts at 900℃ by means of XRD and SEM.Hot-corrosion scale of the superalloy and aluminide diffusion coating were analyzed and their surface morphologies were observed.The results demonstrate that both coated and uncoated specimens are not susceptible to various contents of NaCl.That may be resulted from the Al2O3 scale formation.Growth stress was characterized by the formation of convoluted scales.